Research in depolymerisation of plastics by artificial metal catalysts is relatively recent as most of the earliest studies are related to biocatalytic systems. Metal salts are the conventional catalysts for these processes, wherein acetates, phosphates and chlorides of heavy metals (Ti, Zn, Mg, Co, Fe) or lead oxide are commonly used in the alcoholysis and glycolysis of polyesters [127&#;128]. Despite that these systems ensure high conversions and selectivity, shortcomings relate to the harsh reaction conditions, slow kinetics, cost of metals, toxicity, difficulty in catalyst reusing and need of downstream processing. Significant efforts have thus been made to develop greener and sustainable catalytic systems featuring high efficiency under mild conditions. The use of sodium carbonate or bicarbonate as ecofriendly catalyst replacements for zinc acetate in the glycolysis of PET are examples of this direction [129&#;130]. Recent studies focused on molecular complexes as homogeneous catalysts, whereas heterogeneous systems based on solid-supported metal nanoparticles (NPs) have been scarcely investigated.
In some cases, metal-catalysed depolymerisation processes of PS were described, showing significant selectivity. In an earlier example, thermal treatment of PS waste over a Fe&#;K@Al 2 O 3 catalyst at 400 °C provided a hydrocarbon oil in 92% yield, 71.4% of which were attributable to styrene monomer [ 156 ]. A decrease of 56 kJ mol &#;1 for the activation energy of PS depolymerisation was calculated in the presence of the catalysts. More recently, high-porosity montmorillonite (Mt) was used to prepare Mg-, Zn-, Al-, Cu- or Fe-decorated heterogeneous catalysts [ 157 &#; 158 ]. An oil yield around 89% was obtained at 450 °C over 20% Fe@Mt, composed by 51%, 10% and 6% (wt) styrene, toluene and ethylbenzene, respectively, and additional oligomers.
3.1.3 Polystyrene (PS): PS is a low-cost, hard and brittle plastic used both as a solid or foam in protective packaging, containers and trays [ 151 ]. It is a nonbiodegradable material accounting for about 10% of municipal solid waste [ 135 ]. It is soluble in benzene, carbon disulfide, chlorinated hydrocarbons, lower ethers and N-methyl-2-pyrrolidone (NMP) and has a melting point around 240 °C [ 152 ]. Most methods for PS recycling are not economically advantageous [ 153 ]. Mechanical recycling, based on pelletizing and moulding, produces low-grade plastics with poor mechanical strength and low market value. Solid PS products, such as coffee cups or take-away containers, can be recycled into videocassette cases or office equipment. Incineration at a temperature below °C and insufficient air is believed to produce a mixture of volatile compounds, including hazardous polycyclic aromatic hydrocarbons, alkylbenzenes and benzoperylene [ 154 &#; 155 ]. As for other polymers, pyrolytic methods end up to be poorly selective.
3.1.2 Polybutadiene (PBD): Partial depolymerisation of 1,4-PBD (cis, trans, M w &#; g&#;mol &#;1 ) was achieved by an unconventional tandem ring-opening&#;ring-closing metathesis route mediated by commercially available Ru homogeneous catalysts [ 148 ]. The process afforded C 16 to C 44 mixtures of macrocyclic oligobutadienes with up to 98% selectivity at moderate conversions (59&#;88%) using first-generation Ru complexes bearing a tricyclohexylphosphine (PCy 3 ) ligand, mild reaction temperature (35 °C) but toxic CH 2 Cl 2 solvent ( ). The reaction using second-generation N-heterocyclic carbene ligands was faster and preferably yielded cyclododecatriene. Larger cyclic butadienes may be used in the production of flame retardants, lubricants and specialty polymers [ 149 &#; 150 ].
In a few cases, good selectivity to a liquid fraction was achieved. For instance, nanostructured BaTiO 3 doped with Pb provided a mixture of liquid products, which includes alkanes (73.4%), olefins (22.5%) and naphthalene (4.1%) at total HDPE conversion at 350 °C [ 144 ]. In another example, hydrocracking of PE was performed over Pt NPs supported on SrTiO 3 perovskite nanocuboids [ 145 ]. Virgin PE (M w = &#; g&#;mol &#;1 ) or PE from single-use plastic bags (M w = g&#;mol &#;1 ) was converted in >97% yield into liquid hydrocarbon (alkane) products having a narrow distribution of the molecular weight (960&#; g&#;mol &#;1 ) under 11.7 bar H 2 at 300 °C and solvent-free conditions [ 146 ]. The pyrolysis oils produced may be used as lubricants, waxes or further processed into detergents and cosmetics [ 147 ]. The catalyst could be recycled, however, with reduced performance due to Pt nanoparticle oxidation.
Depolymerisation of PE by catalytic pyrolysis or cracking into liquid fuels was recently reviewed [ 67 , 142 ]. Most of these processes are promoted by heterogeneous acid catalysts (e.g., zeolites, alumina, silica) and are usually unselective, resulting in a broad distribution of gas (C 3 and C 4 hydrocarbons), liquids (cycloparaffins, oligomers, aromatics) and solid products (char, coke) as a consequence of the random scission of C&#;C bonds into radicals, which leads to a complex mixture of olefinic and cross-linked compounds [ 143 ].
3.1.1 Polyethylene (PE): PE is the most used thermoplastic material today, having a variety of uses in several fields. Applications of PE depend on the mechanical and physical properties (particularly the tensile strength, hardness and melting point T m ), which are, in turn, ruled by the molecular weight and degree of branching [ 136 &#; 137 ]. Various types of PE exist, which are classified according to the density, the most common being high-density polyethylene (HDPE) and low-density polyethylene (LDPE). HDPE (0.94&#;0.97 g&#;cm &#;3 , T m 130 °C) is a highly crystalline material with a low degree of short chain branching. Owing to the high stiffness, tensile strength, resistance to moisture and gas permeability, it is mainly used in the manufacture of water pipes, toys, beverage bottles, outdoor furniture, housewares and electrical cables [ 138 &#; 139 ]. LDPE (0.91&#;0.94 g&#;cm &#;3 , T m 120 °C) is a poorly crystalline material having a high degree of short chain and long chain branching. It is featured by a good flexibility, transparency and high impact strength, which make it suitable for short-term applications, such as films, food packaging, squeezable bottles, plastic bags and medical devices [ 140 ]. PEs (except cross-linked samples) are partially soluble in (hot) aromatic hydrocarbons or in chlorinated solvents [ 141 ].
3.2.1 PET: PET is one of the most widely used thermoplastic polyesters, particularly in the textile and food packaging industry (e.g., soft-drink and water bottles, food container, films) due to the excellent thermal and mechanical properties, durability, inertness and transparency. The global production of PET exceeds 50 million tons pear year, while PET accounts for around 8% by weight and 12% by volume of the world's solid waste [159&#;160]. PET is a copolymer of terephthalic acid (TPA) and EG [161]. It is best soluble in chlorophenol, tetrachloroethane, m-cresol, NMP, nitrobenzene and 1,1,1,3,3,3-hexafluoro-2-propanol, insoluble in common alcohols and water and has a melting point of 250 °C and a glass transition temperature Tg of 76 °C [162&#;163]. It was suggested that under certain circumstances, PET may leach phthalates [164], which are known for potentially adverse health effects and subject to ECHA regulation restrictions [165&#;166]. Coupled with the fact that TPA is produced from petrochemical sources, bioderived 2,5-furandicarboxylic acid has been proposed as TPA replacement in the production of plastic bottles, representing one of the rare examples of industrial manufacture of biobased polymers [167&#;168].
From the chemical recycling point of view, PET is one of the most studied plastics, so as to represent a case study in the field [169&#;170]. A variety of added-value, reusable chemicals and monomers can be recovered from PET via chemolytic depolymerisation, including 1,4-benzenedimethanol (BDM), TPA, dimethylterephthalate (DMT), bis(2-hydroxyethyl)terephthalate (BHET), terephthalamides (TPM [171]) and EG ( ). Catalytic hydrogenolysis, hydrolysis, methanolysis and glycolysis reactions of (postconsumer) PET have been reviewed, each showing their own advantages and disadvantages [172&#;173]. For instance, glycolysis usually requires more problematic purifications than methanolysis, which, on the other hand, is generally more energy-intensive. Some solvolytic processes of PET are already in operation at the industrial or pilot scale [174&#;175]. However, they often rely on the use of considerable amounts of strong alkali bases and chlorinated solvents [176&#;177], which makes them neither economically competitive nor environmentally friendly [178&#;179]. A survey of patents related to the chemical recycling of PET up to can be found in the literature [180].
Hydrogenolysis. In the recent years, hydrogenolysis reactions of PET were developed mostly using Ru metal-based catalysts, due to their higher affinity for C=O bond (ester) hydrogenation compared to other metals ( ) [181&#;182]. Thus, a 73% BDM yield was obtained using a soluble Ru(II)&#;PNN complex at 110 °C in THF/anisole solvent, 50 bar of hydrogen and a 20:1 excess of strong base potassium tert-butoxide as cocatalyst ( , entry 1) [183]. Although the reaction mechanism was not investigated in detail, it was suggested that cleavage of the ester linkage may occur in a concerted manner through the reported heterolytic route [184&#;185]. The role of butoxide was postulated to be the activation of the heterogeneous splitting of dihydrogen. BDM is an important building block for the production of resins and polyesters other than PET [186&#;187]. Analogously, a similar Milstein-type ruthenium&#;PNN complex, generated in situ by treatment of the chloride catalyst precursor with potassium butoxide in a 2:1 molar ratio, resulted in a nearly quantitative yield of BDM and EG at a slightly higher reaction temperature (160 °C, 54 bar H2, , entry 2). Interestingly, PET flakes from postconsumer bottles could be used, showing the catalytic system to be resistant to the presence of contaminants and impurities (e.g., additives, pigments) [188]. More recently, effective PET depolymerisation was accomplished by a ruthenium molecular catalysts bearing the well-known tripodal phosphorous ligand 1,1,1-tri(diphenylphosphinomethyl)ethane (triphos) [189&#;190]. Thus, use of Ru(triphos)tmm (tmm = trimethylenemethane) and acidic bis(trifluoromethane)sulfonimide (HNTf2) cocatalyst (1:1) in noxious 1,4-dioxane solvent resulted in 41% PET conversion and 64% BDM selectivity at 140 °C and 100 bar H2 due to the formation of ether byproducts ( , entry 3) [191]. No hypotheses for the reaction mechanism were formulated. Higher conversion (64%) and selectivity (99%) were observed using the bulkier xylyl derivative Ru(triphos-xyl)tmm ( , entry 4), which was attributed to reduced catalyst degradation [192]. The catalyst could be employed for the depolymerisation of PET flakes from various sources (water bottles, dyed soda bottles, pillow filling, yoghurt pots). However, the role of HNTf2 was unclear.
In a different approach, hydrogenolysis-like depolymerisation was achieved through a hydrosilylation strategy, using the pincer Ir(III) complex [Ir(POCOP)H(THF)][B(C6F5)4] (POCOP = 1,3-(t-Bu2PO)2C6H3) as catalyst and an excess of Et3SiH as reagent (chlorobenzene solvent, 70 °C) [193]. BDM could be obtained in an overall 58% yield from PET from fibres or bottles, after hydrolysis of the intermediate silyl ether using Bu4NF·3H2O in THF ( ).
Hydrolysis. Methods for the metal-catalysed hydrolysis of PET were developed, allowing for the recovery of costly TPA monomer ( , top). TPA was obtained in 97.1% yield at full PET conversion, using 70 wt % aqueous ZnCl2 as catalyst at 180 °C and no organic solvent [194]. However, a high ZnCl2/PET weight ratio of 35 was required. The catalyst could be reused, showing significant activity decrease starting from the fourth cycle due to biochar formation. A mechanism was hypothesised in which Zn2+ ions act as a Lewis acid activator for the carbonyl ester bond. In a previous work, complete depolymerisation of PET was achieved using zinc acetate as catalyst in hot compressed water [195]. A TPA yield of 90.5% was obtained at 240 °C after 30 min reaction time, using a ZnAc2/PET weight ratio as low as 0.015. For this, a mechanism was speculated in which proton ions act as activators.
Methanolysis. To the best of our knowledge, only one example of a depolymerisation reaction of PET through alcoholysis was recently reported, which is however devoid of any catalysts [196]. Therein, a 97.3% yield of DMT was obtained at full PET conversion, by treatment of PET with methanol at 200 °C for 3.5 h ( , bottom). No details of byproducts were provided. Ethanol and butanol were much less reactive under identical reaction conditions. The as-prepared DMT could be used for the production of hydrocarbon jet fuels by catalytic hydrogenation. Metal-catalysed methanolysis of PET was described in previous years [109,197].
Glycolysis. Glycolysis is a convenient process for PET chemical recycling, owing to the low cost, relatively mild reaction conditions and the potential for the production of useful monomers and oligomers. These compounds can be used in the synthesis of recycled polyesters, polyurethanes, polyisocyanurates and resins [43]. Among the various glycols, EG is the most popular, resulting in the formation of BHET, formally through a (reversible) transesterification reaction ( ) [198]. Drawbacks of this method are the difficulty of purification of BHET, the need of an excess of EG and the possible product contamination by homogeneous catalysts [199]. The conventional catalysts for this reaction are EG-soluble metal acetates, the activity of which showed a decrease in the order Zn2+ > Mn2+ > Co2+, which was attributed to the diverse interaction between the metal cation promoter and the carbonyl group of polyester [200]. Indeed, several studies showed Zn-based catalysts to provide the best performances. A summary of recent findings and reaction conditions is reported in . In an earlier study, a 85.6% BHET yield was obtained at 196 °C, using an EG/PET ratio of 5:1 (w/w) and 1 wt % Zn(OAc)2 loading ( , entry 1) [201]. The system resulted in partial selectivity to BHET due to the formation of significant amounts of oligomers, mainly BHET dimers, which increased upon standing. The kinetic of the zinc acetate-promoted process was studied over a range of reaction conditions, showing the best combination to be 196 °C, an EG/PET ratio of 2.45:1 (w/w) and a catalyst loading of 0.3 wt % ( , entry 2) [129]. Under these conditions, an equilibrium yield of BHET around 65% was achieved within short reaction times (1 h), much faster than in the absence of catalysts or using alkali salt promoters (Na2CO3, NaHCO3, Na2SO4 or K2SO4, ). PET wastes, including highly coloured and multilayered PET, could be used as substrate. More recently, it was demonstrated that the addition of a cosolvent for PET, such as dimethyl sulfoxide (DMSO), NMP, nitrobenzene or aniline to the conventional PET-insoluble EG system, greatly enhanced the depolymerisation kinetics, resulting in improved conversions (the solubility of PET at T > 130 °C was aniline > NMP > nitrobenzene > DMSO) [202]. For instance, the use of a DMSO/EG 2:1, w/w solvent mixture resulted in an increase of PET conversion from 43.0% to 83.9% compared to pure EG (190 °C, 5 wt % catalyst loading, 5 min reaction time, , entry 4 vs entry 3). Using the same reaction conditions and solvent mixture, Mn, Co, Cu and Ni acetate catalysts were less active than Zn ( , entries 5 and 6). In a further study, glycolysis of PET was performed under microwave heating in the presence of Zn(OAc)2, yielding BHET with an 80% selectivity at 97% conversion due to formation of dimers ( , entry 7) [203&#;204]. Soluble metal chlorides (zinc, magnesium, iron, zirconium, cobalt, nickel) were also explored as catalysts in the glycolytic depolymerisation of PET [128,205]. The highest BHET yield (74.7%) was achieved using zinc chloride (0.5% w/w), an EG/PET ratio of 14:1 and reflux conditions ( , entry 8). The use of preformed soluble Co(II) complexes bearing bidentate phosphorus ligands (e.g., 1,2-bis(dicyclophosphino)ethane) showed minimal improvements compared to the chloride salt catalyst [205]. The use of transition metal-substituted polyoxometallates (POMs), of the general formula K6SiW11MO39(H2O) (M = Zn2+, Mn2+, Co2+, Cu2+, Ni2+) [206&#;207], was also investigated [208]. The catalytic activity was found to decrease in the order Zn > Mn > Co > Cu > Ni, consistent with previous reports [209]. The best catalyst afforded BHET in 84.1% yield ( , entry 9), which was rather constant over eight catalyst reuses [210]. A stepwise depolymerisation mechanism was proposed, via intermediate oligomers, in which Zn ions act as Lewis acid activators for the C=O ester bonds toward nucleophilic attack by EG.
In addition to soluble catalysts, metal-containing insoluble materials, namely solid acid catalysts, were developed for the glycolytic depolymerisation of PET by EG. Representative data are summarised in , wherein the catalyst productivity is reported for comparison as molBHET&#;gcat.&#;1&#;h&#;1. Despite that both catalyst and PET were insoluble in EG at the reaction temperature, most systems displayed substantial activity. Thus, sulfated titania, zinc oxide and mixed oxides (SO42&#;/TiO2, SO42&#;/ZnO and SO42&#;/ZnO&#;TiO2) were prepared, showing the amount of Lewis acid sites and the high surface area of the solid material to be critical in affecting the catalytic efficiency [211]. Best results were obtained for the binary oxide SO42&#;/ZnO&#;TiO2 calcined at 200&#;300 °C (surface area 192 m2&#;g&#;1, density of acidic sites 4.34 mmol&#;g&#;1), which provided BHET in 73% selectivity at full PET conversion at 180 °C reaction temperature and a moderate excess of EG (5.5:1, w/w, , entry 1). The formation of a significant amount of oligomers was detected. The catalyst could be recovered by centrifugation and reused over four cycles with no efficiency decay. Similar effects were reported for Zn-substituted titanate nanotube (TiNT) catalysts [212&#;213]. Therein, a positive role of Zn2+ Lewis acid sites was demonstrated by the higher efficiency compared to the Na+ catalyst counterpart ( , entry 2 vs entry 3), whilst a high surface area around 150 m2&#;g&#;1 was proposed to increase the number of exposed sites [214]. Zn@TiNT afforded BHET in 87% yield at 196 °C reaction temperature. TiNT have received significant general interest in heterogeneous catalysis because of the better active-site-accessibility compared to 2D materials, thanks to a typical 8&#;16 nm outer diameter tubular morphology [215&#;216] and the potential for facile metal doping via ion-exchange of the solid support [217&#;218]. Lewis acid-type catalytic activity was also postulated for γ-Fe2O3 NPs, which provided BHET in 90% yield at 300 °C ( , entry 4) [219]. Therein, thanks to the superparamagnetic properties, easy recovery of the highly dispersed solid catalyst (11 nm size) was possible by application of a magnetic field. The catalyst could be reused over ten cycles without significant activity loss. Other solid-supported nanostructured metal oxides were tested as catalysts for PET glycolysis. Thus, a graphene oxide (GO)&#;Mn3O4 nanocomposite ( , entry 5) [220] and silica NPs-supported Mn3O4 [221] resulted in a good yield of BHET (>90%), however, at a high reaction temperature. A zinc manganite spinel ZnMn2O4 gave BHET in 92% yield at 260 °C and 5 atm pressure ( , entry 6) [222]. On the other hand, amphoteric solid catalysts have also shown usability in EG depolymerisation of PET. For instance, a BHET yield of 75% was achieved over (Mg&#;Zn)&#;Al-layered double hydroxides (LDH) catalysts at 196 °C ( , entry 7) [223]. A cooperative mechanism was proposed in which Lewis acid sites (Mg2+, Al3+, Zn2+) activate the C=O ester bond, while the basic sites (OH&#;) deprotonate EG, enhancing the nucleophilic cleavage of the ester unit [224].
Notably, the depolymerisation of PET by EG was also reported using metal-containing catalysts in the form of ionic liquids (ILs) [209]. Advantages of metallated ILs include low flammability, high thermal stability and versatility. However, their &#;greenness&#; and toxicity are still debated [225&#;226]. Thus, amim[ZnCl3] (amin = 1-allyl-3-methylimidazolium, , entry 1) [227] and amim[ZnCl3] (bmim = 1-butyl-3-methylimidazolium, , entry 2) [228] were recently studied, showing higher catalytic activity compared to metal-free ionic liquids (i.e., bmim chloride), the conventional catalysts (i.e., ZnCl2, Zn(OAc)2) or the analogous Mn, Co and Cu ionic liquids. Typically, 80&#;85% BHET yields were observed for metallated ILs, while under the same experimental conditions, ZnCl2 gave BHET in &#;70% yield ( , entry 5). Similar results were reported for the bmim2[MCl4] (M = Cr, Fe, Co, Zn, Ni, Cu) catalysts, wherein the cobalt derivative resulted in the best performance ( , entry 3) [229]. Based on infrared studies, the higher catalytic activities of the metallated ILs was attributed to their higher Lewis acidity compared to both the metal-free catalysts and the metal salts. A mechanism was therefore proposed in which a synergistic effect of the metallated ILs takes place, based on the activation of the C=O bond by the IL Lewis acid cation and of the hydroxy group in EG by the IL anion ( ). The IL catalysts could be easily separated by distillation and reused up to six times with no significant efficiency drop. Catalytic glycolysis by heterogenised, metallated ionic liquids was also investigated [230], however, showing a lower performance compared to the soluble systems. Thus, PET pellets were fully converted by a bmim[Fe(OAc)3] catalyst immobilised onto bentonite, affording BHET in 44% yield ( , entry 4) [231]. The solid catalyst could be recovered by filtration and reused.
As an alternative to ILs, metal-based deep eutectic solvent (DES) systems were also explored as catalysts for the glycolysis reaction of PET using EG. DES have similar properties to metallated ILs, but they are cheaper and less toxic [232&#;233]. Because of this, they have found application in many fields [234&#;235], though they cannot be considered inherently &#;green&#; [236]. In a recent work, the DES combination zinc acetate and 1,3-dimethylurea (1:4) showed the highest catalytic activity among a series of transition metal acetates (Zn, Mn, Co, Ni, Cu), affording BHET with 82% yield and noticeable productivity (TOF = 129 h&#;1, based on the moles of Zn) at 190°C, EG/PET 4:1, w/w and 5 wt % catalyst [237]. A mechanism was proposed analogous to that depicted in , but in which Zn2+ acts as Lewis acid and dimethylurea acts as base promoter for EG hydroxy deprotonation [238]. The remarkable activity was attributed to the dual effect of base and acid catalysis, in addition to the solubility of the catalyst in EG.
It is worth mentioning that, in addition to the recovery of chemicals via chemolytic processes, repurposing techniques of PET were developed based on one-pot, two-step glycolysis-reprocessing strategies, wherein the depolymerisation products are directly used in a polymerisation reaction, without intermediate purifications. In order to avoid the presence of free glycols in the polymerisation mixture, most of these processes were performed using (sub)stoichiometric amounts of diol cleaving agents, other than EG (for instance, PD [239], DEG [240&#;241]). As a consequence, the depolymerisation step usually results in complex mixtures of oligomers. Moreover, reacting diols may be unstable under the reaction conditions adopted. Hence, if used in excess, a significant formation of decomposition byproducts may be observed (i.e., dioxane and acetaldehyde for DEG [242]). Because of that, these metal-catalysed depolymerisations cannot be strictly considered as selective, although the overall processes are interesting from a practical and sustainability point of view. Some recent examples are cited herein. Postconsumer PET was depolymerised in the melt (at 250 °C) using DEG and Ca/Zn stearate as catalyst, and the product mixture was used in situ in conjunction with bis(2-ethylhexyl)phthalate and the same metal promoter for the production of flexible poly(vinyl chloride) compounds [243]. One-pot depolymerisation&#;polycondensation reactions were developed to produce random copolyesters poly(ethylene terephthalate-co-adipate) from PET in the presence of EG and adipic acid [244]. The depolymerisation step was carried out using a zinc acetate catalyst (1 wt %), with no need of excess of chemicals. Polymerisation was then achieved by raising the reaction temperature, without purification of the intermediate oligomers being required. An interesting one-pot process was developed that combines the use of bioderived chemicals, isosorbide and succinic acid, with PET chemical recycling to produce novel polyesters [245]. In this process, isosorbide was used as depolymerising diol to give a mixture of differently composed oligomers, whereas succinic acid was added in the second step as polymerising comonomer ( ). Both steps were efficiently catalysed by monobutyltin oxide, using substoichiometric amounts of isosorbide and succinic acid and no solvent at 230 °C reaction temperature. Isosorbide is a safe chemical [246] that is obtainable on the large scale from renewable glucose [247&#;248]. Because of this and due to the inherent rigid structure, conferring the resulting polymers with excellent mechanical properties (e.g., stiffness, toughness, hardness), isosorbide is used as monomer in the production of a variety of plastics [249&#;250]. By contrast, the rigidity results in a poor reactivity as depolymerising agent [251].
3.2.2 Polylactic acid (PLA): PLA is a bioderived plastic [252] that is manufactured on a 190 kton scale directly from lactic acid by condensation or from lactide by ring-opening polymerisation ( ) [253&#;254]. The main renewable raw material for lactic acid is starch, e.g., from corn, cassava, sugarcane or beet pulp [255]. Owing to the chirality of lactic acid, three forms of PLA (ʟ, PLLA; &#;, PDLA; &#;ʟ, PDLLA) with slightly different properties (crystallinity, Tg 60&#;65 °C, Tm 130&#;180 °C) exist [256]. PLA is soluble in benzene, tetrahydrofuran, ethyl acetate, propylene carbonate and dioxane [257], and it is biodegradable [258&#;259]. Because of these features, PLA is largely employed in several applications: microelectronics, biomedicine and food packaging [260].
Although chemical recycling of PLA is possible by thermal methods over metal catalysts [261&#;262], these often result in a poor selectivity and in a variety of volatile compounds, with the notable exception of calcium oxide, which gave ʟ,ʟ-lactide from PLLA in &#;98% yield at 250 °C [263].
Alcoholysis. The solvolytic depolymerisation of PLA was mostly reported using zinc-based catalysts, ethanol or methanol agents, wherein a higher reactivity of the latter was ascribed to the better nucleophilicity. Indeed, a methyl lactate (Me-La) and ethyl lactate yield of 70% and 21% was obtained, respectively, using soluble zinc acetate at reflux temperature [264]. Interestingly, under the same reaction conditions, PET was unreactive, thus enabling the selectively recycle of mixed PET/PLA plastic waste. It was suggested that the different reactivity between PLA and PET is attributable to the amorphous, less rigid structure of PLA and to the potential of forming five-membered chetate ring intermediates between Zn(II) ions and lactate units, which favour the transesterification process. More recently, the use of soluble Zn(II) molecular catalysts was investigated. An in-depth study of the methanolysis reaction of PLA was carried out via design of experiments technique, using a series of imino monophenolate&#;Zn complexes and THF solvent. Different commercial samples of PLA were examined, showing the critical operational parameters to be temperature and catalyst concentration, whereas the process was not significantly affected by particle size or stirring speed. Thus, up to 100% Me-La yield was obtained using the six-coordinated Zn(ligand)2 complex sketched in , either at 90 °C and 16 wt % catalyst or 130 °C and 8 wt % catalyst [265]. Higher efficiency was provided by the tetrahedral complex ZnA2 bearing a similar ligand, as shown in ( ), which resulted in 81% Me-La selectivity at full PLA conversion at under 50 °C and 4 wt % catalyst loading [266]. However, in the absence of THF solvent, the latter catalysts gave a 98% Me-La yield at 130 °C. The comparable complexes ZnL12, ZnL22 and ZnL32 shown in resulted in a lower catalytic efficiency (Me-La yield 41&#;88%, 50 °C, 8 wt % catalyst loading, 18 h), and thus indicating a significant steric and electronic effect of the ligand [267]. A reaction mechanism for PLA depolymerisation was proposed, consisting of two consecutive first-order steps, in which Me-La production follows the formation of chain-end groups intermediates [265]. A zinc&#;N-heterocyclic carbene complex was used as catalysts for the methanolysis reaction of PLLA via a two-step, one-pot procedure using CH2Cl2 solvent and an excess of methanol at room temperature ( ) [268]. At full substrate conversion, a Me-La/oligomers ratio around 10:1 was detected by GPC analysis. Notably, mutatis mutandis, almost all of the above described zinc complexes could be used as catalysts, both in PLA alcoholysis and in PLA synthesis via lactide polymerisation.
Metal species other than zinc were reported as effective catalysts for PLA methanolysis. Group 4 metal complexes with salalen ligands of the formula M(ligand)(OiPr)2 (M = Ti, Zr, Hf) were used in the methanolysis reaction of PLA at room temperature with an excess of methanol and CH2Cl2 cosolvent ( ) [269&#;270]. A 75% yield of Me-La and residual oligomers with Mn 500 g&#;mol&#;1 were obtained by conversion of Mn g&#;mol&#;1 PLA using the hafnium derivative. As an alternative to expensive metal (complex) catalysts, methanolysis of PLA was recently described using alkali metal halides [271]. In an optimised experiment, PLA from various goods (cups, fork, spoons, containers, Mw &#; g&#;mol&#;1) was converted into Me-La in up to 97% yield using 2.5 mol % KF, 180 °C microwave heating and 23.1 equiv CH3OH. The potassium fluoride catalyst could be reused in up to three runs with no change in performance, while a 50% drop of the yield was observed afterwards.
Me-La is a low-toxic chemical used as substitute for hydrocarbon solvents, with applications in the field of paints, lacquers and cleaning agents [272&#;273]. It should be finally mentioned that during the alcoholysis reaction of PLA using alkoxide catalysts, alkaline earth metal adducts (typically of Ca2+) were isolated, and thus suggesting a potential involvement of the metal centre in the depolymerisation mechanism [274&#;275].
Hydrogenolysis. The Ru(triphos)tmm/HNTf2 catalytic system described above for the hydrogenolysis reaction of PET was also successfully applied in PLA hydrogenative depolymerisation ( ) [191]. PLA was directly converted to 1,2-propanediol in 99% yield using 1 mol % catalyst (with respect to lactic acid units) and 1,4-dioxane solvent at 140 °C and 100 bar H2. A TOF of 6.19 molPD&#;molRu&#;1&#;h&#;1 can be calculated based on this. Scale-up using PLA granulates and beverage cups was also possible using a lower catalyst loading. In addition, the method allowed for the selective recycle of equimolar mixtures of PET and PLA using the [Ru(triphos-xyl)methylallyl]NTf2 catalyst congener at 45 °C reaction temperature, wherein insoluble PET was filtered out, while PLA was fully converted to PD. Similarly to PET, the ruthenium(II)&#;PNN complex sketched in , entry 2 was also used in PLA hydrogenolysis to give PD in 99% yield at 160 °C, 54 bar H2 and in anisole/THF solvent [182,188]. PD is a safe chemical that is mainly produced from propylene oxide or catalytically from lactic acid intermediate, and it serves in the polymer and food industry or as antifreezing agent [276&#;277].
Under milder reaction conditions, PLA could be converted to the corresponding silyl ether in 92% yield, propane and silicon byproducts (8%) using the above mentioned Brookhart pincer complex [Ir(POCOP)H(THF)][B(C6F5)4] shown in , an excess of Et3SiH and chlorobenzene solvent at 90 °C ( ) [193]. The use of 6 equiv of 1,1,3,3-tetramethyldisiloxane (TMDS) led to the total conversion to propane and polydimethylsiloxane (PDMS), a silicon oil with several applications (lubricants, food-additives, breast implants).
3.2.3 Other polyesters: The hydrogenolysis reaction of esters other than PET and PLA was carried out using the above described soluble Ru(triphos)tmm/HNTf2 catalytic system [191]. Thus, poly(butylene terephthalate) (PBT) and polycaprolactone (PCL) were depolymerised into the corresponding (co)monomeric diols at 140 °C and 100 bar H2 in 1,4-dioxane solvent ( ). A 99% selectivity to 1,6-hexanediol was observed at full PCL conversion, whereas the selectivity to diols was only 22% for PBT (due to the formation of ethers byproducts), which could be raised to 99% by using the bulkier Ru(triphos-xyl)tmm catalyst derivative.
PCL could be converted to 1,6-hexanediol in 68% yield also through a two-step procedure involving hydrosilylation by the above mentioned cationic Ir catalyst complex [Ir(POCOP)H(THF)][B(C6F5)4] and TMDS reagent (chlorobenzene solvent, 90 °C), followed by alkaline hydrolysis (10% NaOH in CH3OH/H2O) [193]. PCL is a biodegradable polymer with a low melting point (&#;60 °C) and glass transition temperature (&#;60 °C). It is commonly used in the manufacture of polyurethanes, to which it imparts improved solvent resistance, flexibility and toughness [278].
The glycolysis of poly(1,4-cyclohexylenedimethylene terephthalate) (PCT) was reported using DEG as reagent and zinc acetate as catalyst (0.12 mol %, ) [279]. A 56% yield of bis(2-hydroxydiethylene terephthalate) (BHDET) was obtained at 196 °C and a DEG/PCT 15:1, w/w ratio, which was five times lower than that using PET under the same reaction conditions. This finding was attributed to the steric hindrance of the 1,4-cyclohexanedimethanol (CHDM)-based chain that hampers the transesterification process. A 90% BHDET yield was achieved using Zn(OCH3)2 catalysts under the same conditions.
Recently, a quantitatively and selectively depolymerisable novel polyester was developed based on a trans-fused six-membered γ-butyrolactone ring, 3,4-T6GBL ( ) [280]. This material joins the advantages of the ease of depolymerisation (97% monomer yield, 180 °C, toluene, 2 mol % ZnCl2 catalyst), rigid structure of the monomer (which provides the polymer with good thermal and mechanical properties) and facile synthesis (ring-opening polymerisation, solvent-free, room temperature, La, Y or Zn catalyst), significantly contributing to a closed-loop concept of plastics recycle. The approach enabled to perform the polymerisation&#;depolymerisation cycle over three times and on a multigram scale, using both linear and cyclic polymers. These advantages are not provided, for example, by more conventional poly(γ-butyrolactone) plastics, which require high depolymerisation temperatures (260&#;300 °C) and undesirable synthetic conditions (&#;40 °C) [281].
Following the same approach to purposely designed, chemically recyclable polymers, it was reported that poly(2-(2-hydroxyethoxybenzoate) (P2HEB) is reversibly depolymerised to 2,3-dihydro-5H-1,4-benzodioxepin-5-one (2,3-DHB) in 94% yield by an aluminium&#;salen catalyst at room temperature ( ) [282]. Thus, a polymerisation&#;depolymerisation cycle could be established using the same metal catalyst, simply by adjusting the initial monomer concentration in a one-pot process.
Metal-catalysed depolymerisation of plastics to reusable building blocks, including monomers, oligomers or added-value chemicals, is an attractive tool for the recycling and valorisation of these materials. The present manuscript shortly reviews the most significant contributions that appeared in the field within the period January &#;January describing selective depolymerisation methods of plastics. Achievements are broken down according to the plastic material, namely polyolefins, polyesters, polycarbonates and polyamides. The focus is on recent advancements targeting sustainable and environmentally friendly processes. Biocatalytic or unselective processes, acid&#;base treatments as well as the production of fuels are not discussed, nor are the methods for the further upgrade of the depolymerisation products.
In a circular-economy perspective, wastes are deemed precious feedstock usable in the production of fertilisers, fuels, chemicals and a variety of materials for packaging, housing, transport and clothing [1,2]. A considerable fraction of the waste currently produced by our society is due to plastics, which is a major problem [3,4]. Plastics are usually synthetic polymers recalcitrant to decomposition, and hence liable to accumulate in landfills or the environment when discarded [5,6]. Not all plastics can be reused, and thus having limited economic value [7,8]. Plastics may release toxic compounds dangerous to human health and the habitat [9,10]. Plastic materials are ubiquitous in our everyday life, which accounts for a global production of plastics of around 360 million tons in [11], of which more than 60% are disposed [12,13]. As a consequence, pollution from plastics is impressive, resulting in the diffusion of microplastics into soil [14,15], oceans [16,17], crustaceans [18] and rain [19].
Valorisation of plastic waste, via chemical conversion into reusable building blocks, may contribute to solving these problems while representing a strategy to reduce the carbon footprint of the chemical industry [20,21]. The approach deepens the concept of plastic recycling [22,23], first of all requiring a careful design of efficient and controlled depolymerisation processes. Despite of this hurdle, the implementation of effective plastics value chains through recovery, reprocessing and upgrade would be a tangible mean to turn a challenge into an opportunity [24,25]. The waste-to-products strategy is already in place for both animal [26,27] and plant biomass polymeric waste [28,29], for which mature technologies are operative [30].
When referring to polymers in general, there is often a lack of univocal definitions, which may lead to confusion between terminologies used as synonyms, though they are not [31,32]. The IUPAC recommendations provide a useful reference to this aim [33]. Thus, &#;degradation&#; is a broad term describing the &#;progressive loss of the performance or of the characteristics of a substance" due to the action of chemical (acids, air, halogens, solvents) or physical agents (heat, light). For polymers, the properties involved are, for instance, tensile strength, colour or shape, the change of which is usually associated with a modification of the chemical composition (e.g., as a consequence of oxidation, cross-linkage, bond cleavage). The term &#;biodegradation&#; indicates a &#;degradation caused by enzymatic processes resulting from the action of cells&#;. Although commonly used, also for artificial polymers, the term &#;biodegradable&#; specifically refers to biorelated polymers (i.e., proteins, nucleic acids, polysaccharides), which are "susceptible to degradation by biological activity by lowering of the molar masses of macromolecules". Therefore, in this situation, &#;chain cleavage&#; and &#;degradation&#; are used interchangeably. To avoid confusion, instead of &#;(bio)degradation&#;, in the present review, we will use the term &#;depolymerisation&#; to identify the &#;process of converting a macromolecule into (recoverable) monomers or a mixture of monomers". Another relevant definition is that of &#;bioplastic&#;, meaning &#;biobased polymer derived from the biomass or issued from monomers derived from the biomass&#;, wherein &#;biobased&#; indicates &#;composed or derived in whole or in part of biological products issued from the biomass&#;. Also, there is no universally accepted definition for &#;compostable&#;, as it differs between diverse issuers [34]. The criteria indicated by the European Commission through the standard EN &#;Packaging&#;Requirements for packaging recoverable through composting and biodegradation&#; include disintegration (i.e., breakdown of material to particles of a defined size), biodegradability, absence of negative effects on the composting process and amount of heavy metals below given maximum values [35,36].
&#;Recycling&#; itself is a general term for which multiple definitions exist, depending on the year and the author [37]. Plastics manufacturers have also delivered their own guidelines under the name &#;Design for Recycling&#; [38,39]. A generally accepted definition for plastic recycling is &#;the process of recovering scrap or waste plastics and reprocessing the material into useful products, sometimes completely different in form from their original state&#; [40,41]. A possible classification of reported plastic recycling techniques is schematically shown in Figure 1 [42], wherein breakdown by the recycled polymer, the final product or the process involved further differentiates between methods, which may lead to occasional overlaps and inconsistencies [43,44].
Figure 1: Potential classification of plastic recycling processes. The area covered by the present review is highlighted in green.
Figure 1: Potential classification of plastic recycling processes. The area covered by the present review is ...
Jump to Figure 1
&#;Reuse&#; is considered a zero-order recycling option, meaning &#;any operation by which products or components that are not waste are used again for the same purpose for which they were conceived&#; [45]. A typical example are plastic containers that are washed and reused as they are [46]. True recycling includes &#;any recovery operation by which waste materials are reprocessed into products, materials or substances whether for the original or other purposes. It includes the reprocessing of organic material but does not include energy recovery and the reprocessing into materials that are to be used as fuels&#; [45]. Therein, three options can be distinguished. &#;Reextrusion&#; (also known as closed-loop recycling) refers to the recycling of clean, uncontaminated single-polymer materials to give products with analogous performance and applications [47]. For example, polyethylene bottles are recycled into new bottles. Similarly, in &#;physical recycling&#;, the polymeric structure of the original material is maintained, although purification steps, the addition of additives or blending with fresh polymers may be included [48]. For this reason, both reextrusion and physical recycling are also referred to as &#;mechanical recycling&#;, primary and secondary, respectively [49,50]. However, materials of lower quality and economic value can be obtained [51,52]. By contrast, the term &#;chemical recycling&#; (or feedstock recycling) refers to those processes involving an alteration of the polymeric chain due to breakage of chemical bonds [53,54]. This definition may be confusing since chain scission may actually occur using either physical (heat) or chemical agents. Indeed, chemical recycling processes can be divided into two main categories: thermochemical and chemolytic routes. All of these processes may result in a variety of valuable products and the mixture thereof, including C1 molecules (CO, CO2, CH4), H2O and H2 due to complete decomposition of the polymeric chain, monomers or oligomers, depending on the waste polymer and the process. The as-obtained compounds can be reused as raw materials for the process industry (hence the term feedstock) to produce chemicals, fuels or other polymers. Thermochemical processes include pyrolysis [55], catalytic cracking [56] and gasification [57]. These are usually unselective, high-temperature treatments (300&#; °C) that may efficiently provide light hydrocarbons or small molecules [58,59]. Chemolytic processes, wherein a chemical reagent is used to achieve depolymerisation, mainly involve solvolysis (a solvent is the reagent and solvolyses include hydrolysis, glycolysis, alcoholysis and aminolysis) and hydrogenolysis reactions (H2 as reagent). Hydrolysis (sometimes called hydrocracking) is in between thermochemical and chemolytic processing, basically consisting of depolymerisation by the combined action of heat and dihydrogen [60]. Chemolytic processes may or may not be catalytic. They will be discussed in detail in the following section. A fourth option is &#;energy recovery&#;. Strictly speaking, this cannot be considered as recycling, consisting in the recovery of the energy contained in a material rather than the material itself, and it is usually achieved by combustion or incineration [61,62]. This method is generally used for plastics that cannot be economically recycled by other means [63,64]. However, it often entails the emission of toxic volatile compounds (furans, dioxins) [65]. The tar obtained may be used for road construction [66].
The present paper shortly reviews the most significant contributions that appeared in the literature, from January to January , in the field of metal-catalysed selective depolymerisation of plastics to reusable monomers, oligomers or added-value chemicals (see Figure 1). Scientific achievements will be described according to the plastic substrate, irrespective of the metal catalyst. Uncatalysed depolymerisations, full chain-cracking or unselective processes, acid&#;base treatments, as well as the production of fuels from plastics, will not be covered. Conversion of plastic waste to fuels [67,68] and biocatalytic depolymerisation methods [69,70] have been extensively and recently reviewed elsewhere, hence they will not be considered herein.
As outlined above, depolymerisation of plastic waste to reusable building blocks is an attractive option for effective recycling and valorisation. This is most conveniently achieved through chemolytic processes because of the higher selectivity and lower energy inputs compared to thermochemical approaches [71]. This is a &#;hot&#; research topic, mainly due to the few industrial applications developed in the field so far, despite the urgent need for innovative technologies that overcome the high costs of recycling, the legal constraints for dumping, the accumulation of plastic scraps and the dependence on nonrenewable (fossil) sources [72,73]. A reason for this underdevelopment is that chemolysis of plastics is still challenging due to multiple critical factors: i) the achievement of selective depolymerisation is only possible by carefully controlled reaction conditions, ii) the related processes must be &#;green&#; and economically viable and, iii) tailored solutions are required to overcome the chemical inertness for, and the thermodynamic limitations of the reversal of each polymer. Indeed, the ease (and outcome) of chain scission does not depend on the origin of the polymer but on its chemical structure [74,75]. For instance, plastics derived from biomass are not necessarily biodegradable, particularly if similar to those obtained from petroleum sources [76,77]. For depolymerisation to be effective at reasonable operating temperature and selective, the plastic substrate should in principle originate from low-exergonic polymerisation reactions [78]. This justifies for the easier depolymerisation of polyesters and polycarbonates compared to polyolefins [79,80]. By contrast, poor selectivity and slow kinetics of depolymerisation can be circumvented using a catalyst.
Several catalytic depolymerisation processes of plastics have been developed, using a solvent or molecular hydrogen as cleaving agents [81]. The main solvolytic process include:
Advantages of catalytic processes are obvious and can be witnessed in the hydrolysis and the glycolysis reactions of poly(ethylene terephthalate) (PET) [82,83]. Representative data are reported in graphical format in Figure 2 for the glycolysis reaction of PET, using titanium(IV) n-butoxide as the catalyst. Compared to the uncatalysed process, benefits include milder reaction conditions, higher selectivity and productivity and reduced generation of waste; in short, improved sustainability [84,85]. However, solvolytic methods are usually not cost-competitive and energy-intensive [86], while they may involve the management of large amounts of noxious solvents and a variety of (decomposition) byproducts [87,88]. Depolymerisation products of course depend on the polymer, the solvent and the reaction conditions. For instance, for polyesters, alcoholysis may provide mixed monomers formally derived from transesterification reactions [89,90], while aminolysis provides amides and alcohols [91,92].
Figure 2: EG produced during glycolytic depolymerisation of PET using DEG + DPG as solvent and titanium(IV) n-butoxide as catalyst. Data from reference [92].
Figure 2: EG produced during glycolytic depolymerisation of PET using DEG + DPG as solvent and titanium(IV) n...
Jump to Figure 2
In the search of &#;greener&#; technologies for plastic recycling, catalytic hydrogenolysis processes have been developed that benefit from the use of H2 as clean reagent and that usually result in a limited number of secondary products [93,94]. The excess of H2 reagent can also be easily removed from the reaction mixture. The approach, referred to as hydrodeoxygenation [95,96], is already in use for the valorisation of naturally-occurring polymeric waste, i.e., lignocellulosic biomass [97,98], particularly lignin [99,100] and cellulose [101], to monomers or added-value platform molecules [102,103]. Here the main drawbacks concern safety hazards, supply, transport and storage costs of hydrogen. Catalytic transfer hydrogenation (CTH) methods from safer reagents have thus been developed and successfully applied to lignocellulose polymers [104,105].
Catalysts of various types, including homogeneous and heterogeneous, have been reported for the above-mentioned depolymerisation processes of plastics. Heterogeneous systems are preferred by industry due to the easier separation from the reaction mixture, reuse and integration into existing reactor equipment [106,107]. Metal-based catalysts have been used for both solvolytic and hydrogenolytic methods, wherein the latter are usually achieved by supported metal species (Ru, Ir), due to the ability to activate molecular hydrogen, functioning as redox centres. The mechanisms of the metal-catalysed solvolytic reactions of plastics are all very similar and typical of conventional organic processes: a metal ion acts as Lewis acid centre for the activation of the chain-linking group of the polymer (either an ester, carbonate, ketone or amide) toward the nucleophilic attack of the various solvents. Specific examples, broken down according to the nature of the polymer and the process, will be reported in the next sections, in which metal catalysts are described in detail. Solvolytic depolymerisations can also be promoted by metal-free soluble acid or base catalysts. However, concentrated solutions, quasistoichiometric amounts or strong mineral acids (HNO3, H2SO4, H3PO4) or bases (NaOH, KOH, potassium butoxide) are often required, particularly for hydrolysis reactions [108,109], which may result in corrosion problems, troublesome neutralisation and purification procedures as well as a considerable generation of waste, which makes these process economically and environmentally unappealing [110,111]. These systems are not considered in the present review.
Biological catalysts for the deconstruction of plastics were extensively studied in the past years, and several hydrolytic-enzymes-containing microorganisms have been shown to be usable for this purpose [112,113]. However, enzymatic depolymerisation is hampered by high molecular weight and crystallinity, reduced chain mobility and hydrophobicity of polymers [114,115], which makes biodegradation often ineffective and time-consuming, particularly for polyolefins, such as polyethylene, polyvinyl chloride (PVC), polystyrene or PET [116,117]. Thus, abiotic pretreatments may be required, including UV irradiation [118], oxidation [119] or acidic degradation [120].
It is worth mentioning that organocatalytic depolymerisation methods have also been reported [121,122]. Despite these systems represent promising &#;greener&#; options, they still are in an early development stage. Uses are mainly limited to nitrogen-based catalysts, ionic liquids [123,124] and alcoholysis of oxygen-containing polymers, such as polyesters, polycarbonates and polyamides, i.e., glycolysis of PET, wherein high temperatures and nearly stoichiometric amounts of catalysts are often required to achieve moderate yields of monomers [125,126].
Research in depolymerisation of plastics by artificial metal catalysts is relatively recent as most of the earliest studies are related to biocatalytic systems. Metal salts are the conventional catalysts for these processes, wherein acetates, phosphates and chlorides of heavy metals (Ti, Zn, Mg, Co, Fe) or lead oxide are commonly used in the alcoholysis and glycolysis of polyesters [127,128]. Despite that these systems ensure high conversions and selectivity, shortcomings relate to the harsh reaction conditions, slow kinetics, cost of metals, toxicity, difficulty in catalyst reusing and need of downstream processing. Significant efforts have thus been made to develop greener and sustainable catalytic systems featuring high efficiency under mild conditions. The use of sodium carbonate or bicarbonate as ecofriendly catalyst replacements for zinc acetate in the glycolysis of PET are examples of this direction [129,130]. Recent studies focused on molecular complexes as homogeneous catalysts, whereas heterogeneous systems based on solid-supported metal nanoparticles (NPs) have been scarcely investigated.
Due to the intrinsic chemical resistance of the hydrocarbon skeleton devoid of functional groups, polyolefins are neither prone to chemical recycling nor biodegradable [131,132]. Hence, they are more commonly repurposed via mechanical recycling, burned or just discarded [133,134]. Depolymerisation of polyolefins usually requires thermal treatments at high temperature [54,135].
3.1.1 Polyethylene (PE): PE is the most used thermoplastic material today, having a variety of uses in several fields. Applications of PE depend on the mechanical and physical properties (particularly the tensile strength, hardness and melting point Tm), which are, in turn, ruled by the molecular weight and degree of branching [136,137]. Various types of PE exist, which are classified according to the density, the most common being high-density polyethylene (HDPE) and low-density polyethylene (LDPE). HDPE (0.94&#;0.97 g&#;cm&#;3, Tm 130 °C) is a highly crystalline material with a low degree of short chain branching. Owing to the high stiffness, tensile strength, resistance to moisture and gas permeability, it is mainly used in the manufacture of water pipes, toys, beverage bottles, outdoor furniture, housewares and electrical cables [138,139]. LDPE (0.91&#;0.94 g&#;cm&#;3, Tm 120 °C) is a poorly crystalline material having a high degree of short chain and long chain branching. It is featured by a good flexibility, transparency and high impact strength, which make it suitable for short-term applications, such as films, food packaging, squeezable bottles, plastic bags and medical devices [140]. PEs (except cross-linked samples) are partially soluble in (hot) aromatic hydrocarbons or in chlorinated solvents [141].
Depolymerisation of PE by catalytic pyrolysis or cracking into liquid fuels was recently reviewed [67,142]. Most of these processes are promoted by heterogeneous acid catalysts (e.g., zeolites, alumina, silica) and are usually unselective, resulting in a broad distribution of gas (C3 and C4 hydrocarbons), liquids (cycloparaffins, oligomers, aromatics) and solid products (char, coke) as a consequence of the random scission of C&#;C bonds into radicals, which leads to a complex mixture of olefinic and cross-linked compounds [143].
In a few cases, good selectivity to a liquid fraction was achieved. For instance, nanostructured BaTiO3 doped with Pb provided a mixture of liquid products, which includes alkanes (73.4%), olefins (22.5%) and naphthalene (4.1%) at total HDPE conversion at 350 °C [144]. In another example, hydrocracking of PE was performed over Pt NPs supported on SrTiO3 perovskite nanocuboids [145]. Virgin PE (Mw = &#; g&#;mol&#;1) or PE from single-use plastic bags (Mw = g&#;mol&#;1) was converted in >97% yield into liquid hydrocarbon (alkane) products having a narrow distribution of the molecular weight (960&#; g&#;mol&#;1) under 11.7 bar H2 at 300 °C and solvent-free conditions [146]. The pyrolysis oils produced may be used as lubricants, waxes or further processed into detergents and cosmetics [147]. The catalyst could be recycled, however, with reduced performance due to Pt nanoparticle oxidation.
3.1.2 Polybutadiene (PBD): Partial depolymerisation of 1,4-PBD (cis, trans, Mw &#; g&#;mol&#;1) was achieved by an unconventional tandem ring-opening&#;ring-closing metathesis route mediated by commercially available Ru homogeneous catalysts [148]. The process afforded C16 to C44 mixtures of macrocyclic oligobutadienes with up to 98% selectivity at moderate conversions (59&#;88%) using first-generation Ru complexes bearing a tricyclohexylphosphine (PCy3) ligand, mild reaction temperature (35 °C) but toxic CH2Cl2 solvent (Scheme 1). The reaction using second-generation N-heterocyclic carbene ligands was faster and preferably yielded cyclododecatriene. Larger cyclic butadienes may be used in the production of flame retardants, lubricants and specialty polymers [149,150].
Scheme 1: Simplified representation of the conversion of 1,4-PBD to C16&#;C44 macrocycles using Ru metathesis catalysts.
Scheme 1: Simplified representation of the conversion of 1,4-PBD to C16&#;C44 macrocycles using Ru metathesis c...
Jump to Scheme 1
3.1.3 Polystyrene (PS): PS is a low-cost, hard and brittle plastic used both as a solid or foam in protective packaging, containers and trays [151]. It is a nonbiodegradable material accounting for about 10% of municipal solid waste [135]. It is soluble in benzene, carbon disulfide, chlorinated hydrocarbons, lower ethers and N-methyl-2-pyrrolidone (NMP) and has a melting point around 240 °C [152]. Most methods for PS recycling are not economically advantageous [153]. Mechanical recycling, based on pelletizing and moulding, produces low-grade plastics with poor mechanical strength and low market value. Solid PS products, such as coffee cups or take-away containers, can be recycled into videocassette cases or office equipment. Incineration at a temperature below °C and insufficient air is believed to produce a mixture of volatile compounds, including hazardous polycyclic aromatic hydrocarbons, alkylbenzenes and benzoperylene [154,155]. As for other polymers, pyrolytic methods end up to be poorly selective.
In some cases, metal-catalysed depolymerisation processes of PS were described, showing significant selectivity. In an earlier example, thermal treatment of PS waste over a Fe&#;K@Al2O3 catalyst at 400 °C provided a hydrocarbon oil in 92% yield, 71.4% of which were attributable to styrene monomer [156]. A decrease of 56 kJ mol&#;1 for the activation energy of PS depolymerisation was calculated in the presence of the catalysts. More recently, high-porosity montmorillonite (Mt) was used to prepare Mg-, Zn-, Al-, Cu- or Fe-decorated heterogeneous catalysts [157,158]. An oil yield around 89% was obtained at 450 °C over 20% Fe@Mt, composed by 51%, 10% and 6% (wt) styrene, toluene and ethylbenzene, respectively, and additional oligomers.
3.2.1 PET: PET is one of the most widely used thermoplastic polyesters, particularly in the textile and food packaging industry (e.g., soft-drink and water bottles, food container, films) due to the excellent thermal and mechanical properties, durability, inertness and transparency. The global production of PET exceeds 50 million tons pear year, while PET accounts for around 8% by weight and 12% by volume of the world's solid waste [159,160]. PET is a copolymer of terephthalic acid (TPA) and EG [161]. It is best soluble in chlorophenol, tetrachloroethane, m-cresol, NMP, nitrobenzene and 1,1,1,3,3,3-hexafluoro-2-propanol, insoluble in common alcohols and water and has a melting point of 250 °C and a glass transition temperature Tg of 76 °C [162,163]. It was suggested that under certain circumstances, PET may leach phthalates [164], which are known for potentially adverse health effects and subject to ECHA regulation restrictions [165,166]. Coupled with the fact that TPA is produced from petrochemical sources, bioderived 2,5-furandicarboxylic acid has been proposed as TPA replacement in the production of plastic bottles, representing one of the rare examples of industrial manufacture of biobased polymers [167,168].
From the chemical recycling point of view, PET is one of the most studied plastics, so as to represent a case study in the field [169,170]. A variety of added-value, reusable chemicals and monomers can be recovered from PET via chemolytic depolymerisation, including 1,4-benzenedimethanol (BDM), TPA, dimethylterephthalate (DMT), bis(2-hydroxyethyl)terephthalate (BHET), terephthalamides (TPM [171]) and EG (Figure 3). Catalytic hydrogenolysis, hydrolysis, methanolysis and glycolysis reactions of (postconsumer) PET have been reviewed, each showing their own advantages and disadvantages [172,173]. For instance, glycolysis usually requires more problematic purifications than methanolysis, which, on the other hand, is generally more energy-intensive. Some solvolytic processes of PET are already in operation at the industrial or pilot scale [174,175]. However, they often rely on the use of considerable amounts of strong alkali bases and chlorinated solvents [176,177], which makes them neither economically competitive nor environmentally friendly [178,179]. A survey of patents related to the chemical recycling of PET up to can be found in the literature [180].
Figure 3: Main added-value monomers obtainable by catalytic depolymerisation of PET via chemolytic methods.
Figure 3: Main added-value monomers obtainable by catalytic depolymerisation of PET via chemolytic methods.
Jump to Figure 3
Hydrogenolysis. In the recent years, hydrogenolysis reactions of PET were developed mostly using Ru metal-based catalysts, due to their higher affinity for C=O bond (ester) hydrogenation compared to other metals (Scheme 2) [181,182]. Thus, a 73% BDM yield was obtained using a soluble Ru(II)&#;PNN complex at 110 °C in THF/anisole solvent, 50 bar of hydrogen and a 20:1 excess of strong base potassium tert-butoxide as cocatalyst (Table 1, entry 1) [183]. Although the reaction mechanism was not investigated in detail, it was suggested that cleavage of the ester linkage may occur in a concerted manner through the reported heterolytic route [184,185]. The role of butoxide was postulated to be the activation of the heterogeneous splitting of dihydrogen. BDM is an important building block for the production of resins and polyesters other than PET [186,187]. Analogously, a similar Milstein-type ruthenium&#;PNN complex, generated in situ by treatment of the chloride catalyst precursor with potassium butoxide in a 2:1 molar ratio, resulted in a nearly quantitative yield of BDM and EG at a slightly higher reaction temperature (160 °C, 54 bar H2, Table 1, entry 2). Interestingly, PET flakes from postconsumer bottles could be used, showing the catalytic system to be resistant to the presence of contaminants and impurities (e.g., additives, pigments) [188]. More recently, effective PET depolymerisation was accomplished by a ruthenium molecular catalysts bearing the well-known tripodal phosphorous ligand 1,1,1-tri(diphenylphosphinomethyl)ethane (triphos) [189,190]. Thus, use of Ru(triphos)tmm (tmm = trimethylenemethane) and acidic bis(trifluoromethane)sulfonimide (HNTf2) cocatalyst (1:1) in noxious 1,4-dioxane solvent resulted in 41% PET conversion and 64% BDM selectivity at 140 °C and 100 bar H2 due to the formation of ether byproducts (Table 1, entry 3) [191]. No hypotheses for the reaction mechanism were formulated. Higher conversion (64%) and selectivity (99%) were observed using the bulkier xylyl derivative Ru(triphos-xyl)tmm (Table 1, entry 4), which was attributed to reduced catalyst degradation [192]. The catalyst could be employed for the depolymerisation of PET flakes from various sources (water bottles, dyed soda bottles, pillow filling, yoghurt pots). However, the role of HNTf2 was unclear.
Scheme 2: Hydrogenolytic depolymerisation of PET by ruthenium complexes.
Scheme 2: Hydrogenolytic depolymerisation of PET by ruthenium complexes.
Jump to Scheme 2
Table 1: Hydrogenolysis of PET by soluble Ru molecular catalysts.
entry catalyst cocatalysta reaction conditionsb conv.c (%) BDM ref. TaCatalyst loading 2 mol %, calculated based on repetition units in PET, cocatalyst molar ratio 2:1. bReaction temperature, hydrogen pressure, reaction time 48 h. cPET conversion. dSelectivity to BDM. eTurnover frequency, calculated based on repetition units in PET and moles of Ru catalyst. fCocatalyst molar ratio 20:1. g1:1 v/v. hCatalyst loading 1 mol %. Reaction time 16 h.
In a different approach, hydrogenolysis-like depolymerisation was achieved through a hydrosilylation strategy, using the pincer Ir(III) complex [Ir(POCOP)H(THF)][B(C6F5)4] (POCOP = 1,3-(t-Bu2PO)2C6H3) as catalyst and an excess of Et3SiH as reagent (chlorobenzene solvent, 70 °C) [193]. BDM could be obtained in an overall 58% yield from PET from fibres or bottles, after hydrolysis of the intermediate silyl ether using Bu4NF·3H2O in THF (Scheme 3).
Scheme 3: Depolymerisation of PET via catalytic hydrosilylation by Ir(III) pincer complex.
Scheme 3: Depolymerisation of PET via catalytic hydrosilylation by Ir(III) pincer complex.
Jump to Scheme 3
Hydrolysis. Methods for the metal-catalysed hydrolysis of PET were developed, allowing for the recovery of costly TPA monomer (Scheme 4, top). TPA was obtained in 97.1% yield at full PET conversion, using 70 wt % aqueous ZnCl2 as catalyst at 180 °C and no organic solvent [194]. However, a high ZnCl2/PET weight ratio of 35 was required. The catalyst could be reused, showing significant activity decrease starting from the fourth cycle due to biochar formation. A mechanism was hypothesised in which Zn2+ ions act as a Lewis acid activator for the carbonyl ester bond. In a previous work, complete depolymerisation of PET was achieved using zinc acetate as catalyst in hot compressed water [195]. A TPA yield of 90.5% was obtained at 240 °C after 30 min reaction time, using a ZnAc2/PET weight ratio as low as 0.015. For this, a mechanism was speculated in which proton ions act as activators.
Scheme 4: Catalytic hydrolysis (top) and methanolysis (bottom) reactions of PET.
Scheme 4: Catalytic hydrolysis (top) and methanolysis (bottom) reactions of PET.
Jump to Scheme 4
Methanolysis. To the best of our knowledge, only one example of a depolymerisation reaction of PET through alcoholysis was recently reported, which is however devoid of any catalysts [196]. Therein, a 97.3% yield of DMT was obtained at full PET conversion, by treatment of PET with methanol at 200 °C for 3.5 h (Scheme 4, bottom). No details of byproducts were provided. Ethanol and butanol were much less reactive under identical reaction conditions. The as-prepared DMT could be used for the production of hydrocarbon jet fuels by catalytic hydrogenation. Metal-catalysed methanolysis of PET was described in previous years [109,197].
Glycolysis. Glycolysis is a convenient process for PET chemical recycling, owing to the low cost, relatively mild reaction conditions and the potential for the production of useful monomers and oligomers. These compounds can be used in the synthesis of recycled polyesters, polyurethanes, polyisocyanurates and resins [43]. Among the various glycols, EG is the most popular, resulting in the formation of BHET, formally through a (reversible) transesterification reaction (Scheme 5) [198]. Drawbacks of this method are the difficulty of purification of BHET, the need of an excess of EG and the possible product contamination by homogeneous catalysts [199]. The conventional catalysts for this reaction are EG-soluble metal acetates, the activity of which showed a decrease in the order Zn2+ > Mn2+ > Co2+, which was attributed to the diverse interaction between the metal cation promoter and the carbonyl group of polyester [200]. Indeed, several studies showed Zn-based catalysts to provide the best performances. A summary of recent findings and reaction conditions is reported in Table 2. In an earlier study, a 85.6% BHET yield was obtained at 196 °C, using an EG/PET ratio of 5:1 (w/w) and 1 wt % Zn(OAc)2 loading (Table 2, entry 1) [201]. The system resulted in partial selectivity to BHET due to the formation of significant amounts of oligomers, mainly BHET dimers, which increased upon standing. The kinetic of the zinc acetate-promoted process was studied over a range of reaction conditions, showing the best combination to be 196 °C, an EG/PET ratio of 2.45:1 (w/w) and a catalyst loading of 0.3 wt % (Table 2, entry 2) [129]. Under these conditions, an equilibrium yield of BHET around 65% was achieved within short reaction times (1 h), much faster than in the absence of catalysts or using alkali salt promoters (Na2CO3, NaHCO3, Na2SO4 or K2SO4, Figure 4). PET wastes, including highly coloured and multilayered PET, could be used as substrate. More recently, it was demonstrated that the addition of a cosolvent for PET, such as dimethyl sulfoxide (DMSO), NMP, nitrobenzene or aniline to the conventional PET-insoluble EG system, greatly enhanced the depolymerisation kinetics, resulting in improved conversions (the solubility of PET at T > 130 °C was aniline > NMP > nitrobenzene > DMSO) [202]. For instance, the use of a DMSO/EG 2:1, w/w solvent mixture resulted in an increase of PET conversion from 43.0% to 83.9% compared to pure EG (190 °C, 5 wt % catalyst loading, 5 min reaction time, Table 2, entry 4 vs entry 3). Using the same reaction conditions and solvent mixture, Mn, Co, Cu and Ni acetate catalysts were less active than Zn (Table 2, entries 5 and 6). In a further study, glycolysis of PET was performed under microwave heating in the presence of Zn(OAc)2, yielding BHET with an 80% selectivity at 97% conversion due to formation of dimers (Table 2, entry 7) [203,204]. Soluble metal chlorides (zinc, magnesium, iron, zirconium, cobalt, nickel) were also explored as catalysts in the glycolytic depolymerisation of PET [128,205]. The highest BHET yield (74.7%) was achieved using zinc chloride (0.5% w/w), an EG/PET ratio of 14:1 and reflux conditions (Table 2, entry 8). The use of preformed soluble Co(II) complexes bearing bidentate phosphorus ligands (e.g., 1,2-bis(dicyclophosphino)ethane) showed minimal improvements compared to the chloride salt catalyst [205]. The use of transition metal-substituted polyoxometallates (POMs), of the general formula K6SiW11MO39(H2O) (M = Zn2+, Mn2+, Co2+, Cu2+, Ni2+) [206,207], was also investigated [208]. The catalytic activity was found to decrease in the order Zn > Mn > Co > Cu > Ni, consistent with previous reports [209]. The best catalyst afforded BHET in 84.1% yield (Table 2, entry 9), which was rather constant over eight catalyst reuses [210]. A stepwise depolymerisation mechanism was proposed, via intermediate oligomers, in which Zn ions act as Lewis acid activators for the C=O ester bonds toward nucleophilic attack by EG.
Scheme 5: Depolymerisation of PET by glycolysis with ethylene glycol.
Scheme 5: Depolymerisation of PET by glycolysis with ethylene glycol.
Jump to Scheme 5
Table 2: Catalytic EG glycolysis of PET by metal acetates or other soluble metal salts.
entry material catalyst EG/PETaaEG as solvent. bReaction temperature. cPET conversion. dSelectivity to BHET. eTurnover frequency calculated based on PET repetition units and moles of metal catalyst. fNot available. gBHET yield (%). hSolvent DMSO/EG 2:1, w/w. iMicrowave irradiation 500 W. jZn polyoxometalate formula K6SiW11ZnO39(H2O).
Figure 4: Glycolysis of PET: evolution of BHET yield over time, with and without zinc acetate catalyst (196 °C, EG/PET ratio 2.45 (w/w). Data from reference [129].
Figure 4: Glycolysis of PET: evolution of BHET yield over time, with and without zinc acetate catalyst (196 °...
Jump to Figure 4
Goto Guangxing to know more.
In addition to soluble catalysts, metal-containing insoluble materials, namely solid acid catalysts, were developed for the glycolytic depolymerisation of PET by EG. Representative data are summarised in Table 3, wherein the catalyst productivity is reported for comparison as molBHET&#;gcat.&#;1&#;h&#;1. Despite that both catalyst and PET were insoluble in EG at the reaction temperature, most systems displayed substantial activity. Thus, sulfated titania, zinc oxide and mixed oxides (SO42&#;/TiO2, SO42&#;/ZnO and SO42&#;/ZnO&#;TiO2) were prepared, showing the amount of Lewis acid sites and the high surface area of the solid material to be critical in affecting the catalytic efficiency [211]. Best results were obtained for the binary oxide SO42&#;/ZnO&#;TiO2 calcined at 200&#;300 °C (surface area 192 m2&#;g&#;1, density of acidic sites 4.34 mmol&#;g&#;1), which provided BHET in 73% selectivity at full PET conversion at 180 °C reaction temperature and a moderate excess of EG (5.5:1, w/w, Table 3, entry 1). The formation of a significant amount of oligomers was detected. The catalyst could be recovered by centrifugation and reused over four cycles with no efficiency decay. Similar effects were reported for Zn-substituted titanate nanotube (TiNT) catalysts [212,213]. Therein, a positive role of Zn2+ Lewis acid sites was demonstrated by the higher efficiency compared to the Na+ catalyst counterpart (Table 3, entry 2 vs entry 3), whilst a high surface area around 150 m2&#;g&#;1 was proposed to increase the number of exposed sites [214]. Zn@TiNT afforded BHET in 87% yield at 196 °C reaction temperature. TiNT have received significant general interest in heterogeneous catalysis because of the better active-site-accessibility compared to 2D materials, thanks to a typical 8&#;16 nm outer diameter tubular morphology [215,216] and the potential for facile metal doping via ion-exchange of the solid support [217,218]. Lewis acid-type catalytic activity was also postulated for γ-Fe2O3 NPs, which provided BHET in 90% yield at 300 °C (Table 3, entry 4) [219]. Therein, thanks to the superparamagnetic properties, easy recovery of the highly dispersed solid catalyst (11 nm size) was possible by application of a magnetic field. The catalyst could be reused over ten cycles without significant activity loss. Other solid-supported nanostructured metal oxides were tested as catalysts for PET glycolysis. Thus, a graphene oxide (GO)&#;Mn3O4 nanocomposite (Table 3, entry 5) [220] and silica NPs-supported Mn3O4 [221] resulted in a good yield of BHET (>90%), however, at a high reaction temperature. A zinc manganite spinel ZnMn2O4 gave BHET in 92% yield at 260 °C and 5 atm pressure (Table 3, entry 6) [222]. On the other hand, amphoteric solid catalysts have also shown usability in EG depolymerisation of PET. For instance, a BHET yield of 75% was achieved over (Mg&#;Zn)&#;Al-layered double hydroxides (LDH) catalysts at 196 °C (Table 2, entry 7) [223]. A cooperative mechanism was proposed in which Lewis acid sites (Mg2+, Al3+, Zn2+) activate the C=O ester bond, while the basic sites (OH&#;) deprotonate EG, enhancing the nucleophilic cleavage of the ester unit [224].
Table 3: Glycolysis of PET using EG and insoluble, solid-supported metal catalysts.
entry material catalyst EG/PETaReaction temperature. bPET conversion. cSelectivity to BHET. dCatalyst productivity calculated based on PET repetition units, moles of BHET and grams of solid catalyst.
Notably, the depolymerisation of PET by EG was also reported using metal-containing catalysts in the form of ionic liquids (ILs) [209]. Advantages of metallated ILs include low flammability, high thermal stability and versatility. However, their &#;greenness&#; and toxicity are still debated [225,226]. Thus, amim[ZnCl3] (amin = 1-allyl-3-methylimidazolium, Table 4, entry 1) [227] and amim[ZnCl3] (bmim = 1-butyl-3-methylimidazolium, Table 4, entry 2) [228] were recently studied, showing higher catalytic activity compared to metal-free ionic liquids (i.e., bmim chloride), the conventional catalysts (i.e., ZnCl2, Zn(OAc)2) or the analogous Mn, Co and Cu ionic liquids. Typically, 80&#;85% BHET yields were observed for metallated ILs, while under the same experimental conditions, ZnCl2 gave BHET in &#;70% yield (Table 4, entry 5). Similar results were reported for the bmim2[MCl4] (M = Cr, Fe, Co, Zn, Ni, Cu) catalysts, wherein the cobalt derivative resulted in the best performance (Table 4, entry 3) [229]. Based on infrared studies, the higher catalytic activities of the metallated ILs was attributed to their higher Lewis acidity compared to both the metal-free catalysts and the metal salts. A mechanism was therefore proposed in which a synergistic effect of the metallated ILs takes place, based on the activation of the C=O bond by the IL Lewis acid cation and of the hydroxy group in EG by the IL anion (Scheme 6). The IL catalysts could be easily separated by distillation and reused up to six times with no significant efficiency drop. Catalytic glycolysis by heterogenised, metallated ionic liquids was also investigated [230], however, showing a lower performance compared to the soluble systems. Thus, PET pellets were fully converted by a bmim[Fe(OAc)3] catalyst immobilised onto bentonite, affording BHET in 44% yield (Table 4, entry 4) [231]. The solid catalyst could be recovered by filtration and reused.
Table 4: Catalytic EG glycolysis of PET using metallated ionic liquids.
entry catalyst EG/PETaReaction temperature. bPET conversion. cSelectivity to BHET. dTurnover frequency calculated based on PET repetition units and moles of metal catalyst. eLoading of bmim[Fe(OAc)3] immobilised onto bentonite. fCalculated with respect to the moles of iron. gMetal salt.
Scheme 6: Potential activated complex for the glycolysis reaction of PET catalysed by metallated ILs and evolution toward products.
Scheme 6: Potential activated complex for the glycolysis reaction of PET catalysed by metallated ILs and evol...
Jump to Scheme 6
As an alternative to ILs, metal-based deep eutectic solvent (DES) systems were also explored as catalysts for the glycolysis reaction of PET using EG. DES have similar properties to metallated ILs, but they are cheaper and less toxic [232,233]. Because of this, they have found application in many fields [234,235], though they cannot be considered inherently &#;green&#; [236]. In a recent work, the DES combination zinc acetate and 1,3-dimethylurea (1:4) showed the highest catalytic activity among a series of transition metal acetates (Zn, Mn, Co, Ni, Cu), affording BHET with 82% yield and noticeable productivity (TOF = 129 h&#;1, based on the moles of Zn) at 190°C, EG/PET 4:1, w/w and 5 wt % catalyst [237]. A mechanism was proposed analogous to that depicted in Scheme 6, but in which Zn2+ acts as Lewis acid and dimethylurea acts as base promoter for EG hydroxy deprotonation [238]. The remarkable activity was attributed to the dual effect of base and acid catalysis, in addition to the solubility of the catalyst in EG.
It is worth mentioning that, in addition to the recovery of chemicals via chemolytic processes, repurposing techniques of PET were developed based on one-pot, two-step glycolysis-reprocessing strategies, wherein the depolymerisation products are directly used in a polymerisation reaction, without intermediate purifications. In order to avoid the presence of free glycols in the polymerisation mixture, most of these processes were performed using (sub)stoichiometric amounts of diol cleaving agents, other than EG (for instance, PD [239], DEG [240,241]). As a consequence, the depolymerisation step usually results in complex mixtures of oligomers. Moreover, reacting diols may be unstable under the reaction conditions adopted. Hence, if used in excess, a significant formation of decomposition byproducts may be observed (i.e., dioxane and acetaldehyde for DEG [242]). Because of that, these metal-catalysed depolymerisations cannot be strictly considered as selective, although the overall processes are interesting from a practical and sustainability point of view. Some recent examples are cited herein. Postconsumer PET was depolymerised in the melt (at 250 °C) using DEG and Ca/Zn stearate as catalyst, and the product mixture was used in situ in conjunction with bis(2-ethylhexyl)phthalate and the same metal promoter for the production of flexible poly(vinyl chloride) compounds [243]. One-pot depolymerisation&#;polycondensation reactions were developed to produce random copolyesters poly(ethylene terephthalate-co-adipate) from PET in the presence of EG and adipic acid [244]. The depolymerisation step was carried out using a zinc acetate catalyst (1 wt %), with no need of excess of chemicals. Polymerisation was then achieved by raising the reaction temperature, without purification of the intermediate oligomers being required. An interesting one-pot process was developed that combines the use of bioderived chemicals, isosorbide and succinic acid, with PET chemical recycling to produce novel polyesters [245]. In this process, isosorbide was used as depolymerising diol to give a mixture of differently composed oligomers, whereas succinic acid was added in the second step as polymerising comonomer (Scheme 7). Both steps were efficiently catalysed by monobutyltin oxide, using substoichiometric amounts of isosorbide and succinic acid and no solvent at 230 °C reaction temperature. Isosorbide is a safe chemical [246] that is obtainable on the large scale from renewable glucose [247,248]. Because of this and due to the inherent rigid structure, conferring the resulting polymers with excellent mechanical properties (e.g., stiffness, toughness, hardness), isosorbide is used as monomer in the production of a variety of plastics [249,250]. By contrast, the rigidity results in a poor reactivity as depolymerising agent [251].
Scheme 7: One-pot, two-step process for PET repurposing via chemical recycling.
Scheme 7: One-pot, two-step process for PET repurposing via chemical recycling.
Jump to Scheme 7
3.2.2 Polylactic acid (PLA): PLA is a bioderived plastic [252] that is manufactured on a 190 kton scale directly from lactic acid by condensation or from lactide by ring-opening polymerisation (Scheme 8) [253,254]. The main renewable raw material for lactic acid is starch, e.g., from corn, cassava, sugarcane or beet pulp [255]. Owing to the chirality of lactic acid, three forms of PLA (ʟ, PLLA; &#;, PDLA; &#;ʟ, PDLLA) with slightly different properties (crystallinity, Tg 60&#;65 °C, Tm 130&#;180 °C) exist [256]. PLA is soluble in benzene, tetrahydrofuran, ethyl acetate, propylene carbonate and dioxane [257], and it is biodegradable [258,259]. Because of these features, PLA is largely employed in several applications: microelectronics, biomedicine and food packaging [260].
Although chemical recycling of PLA is possible by thermal methods over metal catalysts [261,262], these often result in a poor selectivity and in a variety of volatile compounds, with the notable exception of calcium oxide, which gave ʟ,ʟ-lactide from PLLA in &#;98% yield at 250 °C [263].
Alcoholysis. The solvolytic depolymerisation of PLA was mostly reported using zinc-based catalysts, ethanol or methanol agents, wherein a higher reactivity of the latter was ascribed to the better nucleophilicity. Indeed, a methyl lactate (Me-La) and ethyl lactate yield of 70% and 21% was obtained, respectively, using soluble zinc acetate at reflux temperature [264]. Interestingly, under the same reaction conditions, PET was unreactive, thus enabling the selectively recycle of mixed PET/PLA plastic waste. It was suggested that the different reactivity between PLA and PET is attributable to the amorphous, less rigid structure of PLA and to the potential of forming five-membered chetate ring intermediates between Zn(II) ions and lactate units, which favour the transesterification process. More recently, the use of soluble Zn(II) molecular catalysts was investigated. An in-depth study of the methanolysis reaction of PLA was carried out via design of experiments technique, using a series of imino monophenolate&#;Zn complexes and THF solvent. Different commercial samples of PLA were examined, showing the critical operational parameters to be temperature and catalyst concentration, whereas the process was not significantly affected by particle size or stirring speed. Thus, up to 100% Me-La yield was obtained using the six-coordinated Zn(ligand)2 complex sketched in Scheme 9a, either at 90 °C and 16 wt % catalyst or 130 °C and 8 wt % catalyst [265]. Higher efficiency was provided by the tetrahedral complex ZnA2 bearing a similar ligand, as shown in (Scheme 9b), which resulted in 81% Me-La selectivity at full PLA conversion at under 50 °C and 4 wt % catalyst loading [266]. However, in the absence of THF solvent, the latter catalysts gave a 98% Me-La yield at 130 °C. The comparable complexes ZnL12, ZnL22 and ZnL32 shown in Scheme 9c resulted in a lower catalytic efficiency (Me-La yield 41&#;88%, 50 °C, 8 wt % catalyst loading, 18 h), and thus indicating a significant steric and electronic effect of the ligand [267]. A reaction mechanism for PLA depolymerisation was proposed, consisting of two consecutive first-order steps, in which Me-La production follows the formation of chain-end groups intermediates [265]. A zinc&#;N-heterocyclic carbene complex was used as catalysts for the methanolysis reaction of PLLA via a two-step, one-pot procedure using CH2Cl2 solvent and an excess of methanol at room temperature (Scheme 10) [268]. At full substrate conversion, a Me-La/oligomers ratio around 10:1 was detected by GPC analysis. Notably, mutatis mutandis, almost all of the above described zinc complexes could be used as catalysts, both in PLA alcoholysis and in PLA synthesis via lactide polymerisation.
Scheme 9: Structures of the zinc molecular catalysts used for PLA-methanolysis in various works. a) See [265], b) see [266], c) see [267].
Scheme 9: Structures of the zinc molecular catalysts used for PLA-methanolysis in various works. a) See [265], b) ...
Jump to Scheme 9
Scheme 10: Depolymerisation of PLLA by Zn&#;N-heterocyclic carbene complex.
Scheme 10: Depolymerisation of PLLA by Zn&#;N-heterocyclic carbene complex.
Jump to Scheme 10
Metal species other than zinc were reported as effective catalysts for PLA methanolysis. Group 4 metal complexes with salalen ligands of the formula M(ligand)(OiPr)2 (M = Ti, Zr, Hf) were used in the methanolysis reaction of PLA at room temperature with an excess of methanol and CH2Cl2 cosolvent (Scheme 11) [269,270]. A 75% yield of Me-La and residual oligomers with Mn 500 g&#;mol&#;1 were obtained by conversion of Mn g&#;mol&#;1 PLA using the hafnium derivative. As an alternative to expensive metal (complex) catalysts, methanolysis of PLA was recently described using alkali metal halides [271]. In an optimised experiment, PLA from various goods (cups, fork, spoons, containers, Mw &#; g&#;mol&#;1) was converted into Me-La in up to 97% yield using 2.5 mol % KF, 180 °C microwave heating and 23.1 equiv CH3OH. The potassium fluoride catalyst could be reused in up to three runs with no change in performance, while a 50% drop of the yield was observed afterwards.
Me-La is a low-toxic chemical used as substitute for hydrocarbon solvents, with applications in the field of paints, lacquers and cleaning agents [272,273]. It should be finally mentioned that during the alcoholysis reaction of PLA using alkoxide catalysts, alkaline earth metal adducts (typically of Ca2+) were isolated, and thus suggesting a potential involvement of the metal centre in the depolymerisation mechanism [274,275].
Hydrogenolysis. The Ru(triphos)tmm/HNTf2 catalytic system described above for the hydrogenolysis reaction of PET was also successfully applied in PLA hydrogenative depolymerisation (Scheme 12) [191]. PLA was directly converted to 1,2-propanediol in 99% yield using 1 mol % catalyst (with respect to lactic acid units) and 1,4-dioxane solvent at 140 °C and 100 bar H2. A TOF of 6.19 molPD&#;molRu&#;1&#;h&#;1 can be calculated based on this. Scale-up using PLA granulates and beverage cups was also possible using a lower catalyst loading. In addition, the method allowed for the selective recycle of equimolar mixtures of PET and PLA using the [Ru(triphos-xyl)methylallyl]NTf2 catalyst congener at 45 °C reaction temperature, wherein insoluble PET was filtered out, while PLA was fully converted to PD. Similarly to PET, the ruthenium(II)&#;PNN complex sketched in Table 1, entry 2 was also used in PLA hydrogenolysis to give PD in 99% yield at 160 °C, 54 bar H2 and in anisole/THF solvent [182,188]. PD is a safe chemical that is mainly produced from propylene oxide or catalytically from lactic acid intermediate, and it serves in the polymer and food industry or as antifreezing agent [276,277].
Under milder reaction conditions, PLA could be converted to the corresponding silyl ether in 92% yield, propane and silicon byproducts (8%) using the above mentioned Brookhart pincer complex [Ir(POCOP)H(THF)][B(C6F5)4] shown in Scheme 3, an excess of Et3SiH and chlorobenzene solvent at 90 °C (Scheme 13) [193]. The use of 6 equiv of 1,1,3,3-tetramethyldisiloxane (TMDS) led to the total conversion to propane and polydimethylsiloxane (PDMS), a silicon oil with several applications (lubricants, food-additives, breast implants).
3.2.3 Other polyesters: The hydrogenolysis reaction of esters other than PET and PLA was carried out using the above described soluble Ru(triphos)tmm/HNTf2 catalytic system [191]. Thus, poly(butylene terephthalate) (PBT) and polycaprolactone (PCL) were depolymerised into the corresponding (co)monomeric diols at 140 °C and 100 bar H2 in 1,4-dioxane solvent (Scheme 14). A 99% selectivity to 1,6-hexanediol was observed at full PCL conversion, whereas the selectivity to diols was only 22% for PBT (due to the formation of ethers byproducts), which could be raised to 99% by using the bulkier Ru(triphos-xyl)tmm catalyst derivative.
Scheme 14: Hydrogenative depolymerisation of PBT and PCL by molecular Ru catalysts.
Scheme 14: Hydrogenative depolymerisation of PBT and PCL by molecular Ru catalysts.
Jump to Scheme 14
PCL could be converted to 1,6-hexanediol in 68% yield also through a two-step procedure involving hydrosilylation by the above mentioned cationic Ir catalyst complex [Ir(POCOP)H(THF)][B(C6F5)4] and TMDS reagent (chlorobenzene solvent, 90 °C), followed by alkaline hydrolysis (10% NaOH in CH3OH/H2O) [193]. PCL is a biodegradable polymer with a low melting point (&#;60 °C) and glass transition temperature (&#;60 °C). It is commonly used in the manufacture of polyurethanes, to which it imparts improved solvent resistance, flexibility and toughness [278].
The glycolysis of poly(1,4-cyclohexylenedimethylene terephthalate) (PCT) was reported using DEG as reagent and zinc acetate as catalyst (0.12 mol %, Scheme 15) [279]. A 56% yield of bis(2-hydroxydiethylene terephthalate) (BHDET) was obtained at 196 °C and a DEG/PCT 15:1, w/w ratio, which was five times lower than that using PET under the same reaction conditions. This finding was attributed to the steric hindrance of the 1,4-cyclohexanedimethanol (CHDM)-based chain that hampers the transesterification process. A 90% BHDET yield was achieved using Zn(OCH3)2 catalysts under the same conditions.
Scheme 15: Glycolysis reaction of PCT by diethylene glycol.
Scheme 15: Glycolysis reaction of PCT by diethylene glycol.
Jump to Scheme 15
Recently, a quantitatively and selectively depolymerisable novel polyester was developed based on a trans-fused six-membered γ-butyrolactone ring, 3,4-T6GBL (Scheme 16) [280]. This material joins the advantages of the ease of depolymerisation (97% monomer yield, 180 °C, toluene, 2 mol % ZnCl2 catalyst), rigid structure of the monomer (which provides the polymer with good thermal and mechanical properties) and facile synthesis (ring-opening polymerisation, solvent-free, room temperature, La, Y or Zn catalyst), significantly contributing to a closed-loop concept of plastics recycle. The approach enabled to perform the polymerisation&#;depolymerisation cycle over three times and on a multigram scale, using both linear and cyclic polymers. These advantages are not provided, for example, by more conventional poly(γ-butyrolactone) plastics, which require high depolymerisation temperatures (260&#;300 °C) and undesirable synthetic conditions (&#;40 °C) [281].
Following the same approach to purposely designed, chemically recyclable polymers, it was reported that poly(2-(2-hydroxyethoxybenzoate) (P2HEB) is reversibly depolymerised to 2,3-dihydro-5H-1,4-benzodioxepin-5-one (2,3-DHB) in 94% yield by an aluminium&#;salen catalyst at room temperature (Scheme 17) [282]. Thus, a polymerisation&#;depolymerisation cycle could be established using the same metal catalyst, simply by adjusting the initial monomer concentration in a one-pot process.
3.3.1 Poly(bisphenol A carbonate) (PBPAC): Bisphenol A (BPA) is a monomer for a variety of polymers widespread in our everyday life, namely polycarbonates, polyesters, polyethers, polysulphones and epoxy resins [249,283]. Particularly, PBPAC is used in the manufacture of plastics for food and beverage containers, safety helmets, optical lenses, electronic and medical equipment, phones, automotive components and toys [284,285]. This justifies for BPA to be one of the highest-volume chemicals produced worldwide, with a global market of around 6 million tons in , 68% of which account for the manufacture of polycarbonates [286,287]. However, BPA is considered a hazardous substance [288,289] and an endocrine disrupting agent [290,291]. BPA can leach from the corresponding polymers, including water- and temperature-sensitive polycarbonates [292,293]. BPA is industrially obtained by the condensation reaction of phenol with acetone, using an excess of phenol [294]. All byproducts of the process, including unreacted phenol, are toxic [295,296], whereas a purity greater than 98% is required for most BPA applications [297,298]. PBPAC is then produced by the condensation of BPA and a carbonyl source, usually phosgene or diphenyl carbonate [299,300]. Commercial PBPAC is a tough material with an average Mw of g&#;mol&#;1 and Tg around 150 °C. It is soluble in THF, hazardous NMP and chlorinated solvents and insoluble in alcohols and water [301]. A number of chemolytic processes have been developed in the recent years for the selective depolymerisation of PBPAC, including hydrogenolysis, hydrolysis, alcoholysis and aminolysis, some of which are metal-catalysed [302,303].
Hydrogenolysis. The hydrogenative depolymerisation of PBPAC was accomplished through the Ru&#;triphos molecular catalyst described above for PET, PLA, PBT and PCL polyesters [191]. Thus, use of the soluble Ru(triphos)tmm complex, in conjunction with acid HNTf2 cocatalyst (1:1) in 1,4-dioxane, resulted in complete conversion and selectivity to BPA and methanol under the moderate conditions of using 100 bar H2 at 140 °C (Scheme 18 and Table 5, entry 1). The protocol could be successfully extended to the depolymerisation of consumer goods, such as compact discs and beverage cups. Notably, pure BPA could be recovered in >70% yield after simple CH2Cl2 extraction. A similar approach was recently reported using commercially available Ru(II) catalysts, namely the Milstein [304] and the Ru&#;MACHO&#;BH [305] complexes bearing tridentate PN ligands, as shown in Table 5, entries 2 and 3, which are known as efficient hydrogenation catalysts of organic carbonates [306,307]. High BPA yields were obtained in those experiments as well, though with lower hydrogen pressure and catalyst productivity in terms of turnover frequency (molBPA&#;molRu cat.&#;1&#;h&#;1). Potassium tert-butoxide was used as cocatalyst, the role of which was speculated to activate the carbonate group of the polymer [308]. The depolymerisation of a digital versatile disc (DVD) using the latter catalyst afforded BPA in an estimated 97% yield after THF pretreatment.
Scheme 18: Hydrogenative depolymerisation of PBPAC by molecular Ru catalysts.
Scheme 18: Hydrogenative depolymerisation of PBPAC by molecular Ru catalysts.
Jump to Scheme 18
Table 5: Hydrogenolysis of PBPAC by soluble Ru molecular catalysts.
entry catalyst cocatalysta reaction conditionsb conv.caCatalyst loading 5 mol %, calculated based on PBPAC repetition units, cocatalyst molar ratio = 1:1. bReaction temperature, hydrogen pressure, 24 h reaction time. cPBPAC conversion. dSelectivity to BPA. eTurnover frequency, calculated based on PBPAC repetition units and moles of Ru catalyst. fCatalyst loading 1 mol %. gReaction time 16 h.
Hydrolysis. The hydrolytic depolymerisation of PBPAC in hot compressed water was achieved via manganese acetate catalyst (Scheme 19, top) [309]. Under optimal conditions (280 °C, catalyst loading 2 wt %), the reaction resulted in 55% selectivity to BPA and 19% to phenol at full polymer conversion. A higher selectivity to BPA was obtained by simple Lewis acid treatment using rare earth metal triflate catalysts [310]. The process occurred in the homogeneous phase using a THF/H2O solvent mixture and a H2O/PBPAC weight ratio of &#;1. The highest BPA yield (97% at 160 °C) was observed for La(CF3SO3)3 due to the reduced decomposition of BPA to phenol, 4-isopropenylphenol and 4-isopropylphenol. A comparison with triflic acid catalyst ruled out the possibility of a proton-catalysed depolymerisation process.
Scheme 19: Catalytic hydrolysis (top), alcoholysis (middle) and aminolysis (bottom) reactions of PBPAC.
Scheme 19: Catalytic hydrolysis (top), alcoholysis (middle) and aminolysis (bottom) reactions of PBPAC.
Jump to Scheme 19
Alcoholysis. A variety of metal-based catalytic systems was recently described for the alcoholysis reaction of PBPAC using diverse alcohols (Scheme 19, middle). Thus, a Lewis acid catalyst consisting of a soluble FeCl3&#;ionic liquid adduct, namely BmimCl·2FeCl3, was reported for the methanolysis of PBPAC, providing BPA in 97% yield at 120 °C [311]. Higher alcohols resulted in lower BPA yields. A mechanism was hypothesised in which the iron centre activates the carbonyl group of the polymer toward nucleophilic attack of methanol. The catalyst could be efficiently recovered and reused over six runs, after ethyl acetate/water extraction. On the other hand, CeO2&#;CaO particles onto hollow ZrO2 nanospheres were used as heterogeneous catalyst for the methanolysis of PBPAC, yielding around 95% BPA at 100 °C in a THF/methanol mixture [312]. The basic sites, due to lattice O2&#; of CeO2, were attributed to be responsible for the deprotonation of methanol, and thus initiating the solvolytic process in that reaction. Depolymerisation of PBPAC was reported using various alcohols (methanol, phenol, benzyl alcohol, 1-naphthol, PD, glycerol), a mechanical mixture of zinc oxide NPs and tetrabutylammonium chloride as catalyst as well as THF cosolvent to give BPA and the corresponding carbonates in >98% yield at 100 °C reaction temperature (Scheme 19) [313]. The insoluble Lewis acid ZnO catalyst could be removed from the reaction mixture by centrifugation and reused five times with a minor loss of activity. However, Bu4NCl was only partially recovered and had to be integrated with fresh cocatalyst after each run. Remarkably, the reaction with glycerol enabled the recycling of two industrial wastes (PBPAC and glycerol) into the valuable chemicals BPA and glycerol carbonate in one process only, with the latter compound being industrially used as synthetic intermediate, solvent and in the formulation of cosmetics [314].
Aminolysis. The ZnO&#;Bu4NCl Lewis acid catalytic mixture was also successfully used in the aminolytic depolymerisation of PBPAC by different amines (cyclohexylamine, aniline, imidazole, 1,2-diaminopropane, 1,3-diaminopropane) to give the corresponding substituted (cyclic) ureas in >97% yield (Scheme 19, bottom) [313]. The reaction with 2-amino-1-propanol gave 4-methyloxazolidin-2-one. Despite the complications due to separation from BPA, the process provides ureas of industrial relevance as anticancer or antiviral agents [315,316].
3.3.2 Poly(propylene carbonate) (PPC) and poly(ethylene carbonate) (PEC): PPC is a thermoplastic material obtained by the copolymerisation of CO2 with propylene oxide or propylenediol, which is mainly used as a packing material and in binder applications [317]. It has a low thermal stability, with a decomposition temperature around 200 °C and a Tg around 40 °C, depending on the molecular weight. PPC may be readily dissolved in many solvents (e.g., chlorinated hydrocarbons, THF, benzene, ethyl acetate and lower ketones), but it is insoluble in longer-chain alkanes, alcohols and water [318].
Hydrogenative depolymerisation of PPC and PEC to methanol and the respective glycols (PD and EG, respectively) was achieved using the soluble Milstein ruthenium catalysts described above for the hydrogenolysis of PET (Scheme 20) [188]. Thus, more than 91% glycol yield was obtained using a 1:2 Ru catalyst/butoxide molar ratio, 160 °C reaction temperature, 55 bar H2 pressure and an anisole/THF 1:1 solvent mixture (Table 6, entries 1 and 2). The same approach was adopted using a Ru(II)&#;PNP pincer complex, showing higher catalytic activity (TOF 41.3 h&#;1) under similar reaction conditions (Table 6, entry 3) [319]. The role of butoxide was proposed to be the conversion of the staring molecular complex in the catalytically active species by elimination of HCl. Similarly, a nonprecious PNN&#;manganese carbonyl complex was reported to afford PD from PPC in 91% yield (Table 6, entry 4) [320]. By contrast, use of a comparable Mn complex and KH as activator resulted in a much lower selectivity to PD (68%) at full PPC conversion (110 °C, 50 bar H2, in toluene), resulting in the formation of a propylene carbonate byproduct [321].
Scheme 20: Hydrogenative depolymerisation of PPC (top) and PEC (bottom) by molecular Ru catalysts.
Scheme 20: Hydrogenative depolymerisation of PPC (top) and PEC (bottom) by molecular Ru catalysts.
Jump to Scheme 20
Table 6: Hydrogenolysis of PPC by molecular metal catalysts.
entry catalyst cocatalysta reaction conditionsb conv.caCatalyst loading 1 mol %, calculated based on PPC repetition units, cocatalyst molar ratio = 2:1. bReaction temperature, hydrogen pressure, 24 h reaction time. cPPC conversion. dSelectivity to PD. eTurnover frequency, calculated based on PPC repetition units and moles of Ru catalyst. f1:1, v/v. gCatalyst loading 0.1 mol %, cocatalyst molar ratio = 1:1. hCatalyst loading 0.2 mol %, cocatalyst molar ratio = 2:1. iReaction time 16 h. jCatalytic hydrogen transfer. Catalyst loading 5 mol %, cocatalyst molar ratio = 1:1, reaction time 30 h. k4:1, v/v.
In the search of safer and &#;greener&#; alternatives, a slightly different approach to controlled PPC depolymerisation was recently proposed, based on catalytic hydrogen transfer rather than hydrogenation reaction, and thus to avoid involvement of high H2 pressures [322]. Thus, hydrogen transfer from isopropanol to PPC using a soluble iron pincer-type catalyst resulted in a 65% PD yield at 140 °C (Table 6, entry 5). However, a relatively high amount of catalyst was required. Potassium butoxide and THF were used as precatalyst activator and cosolvent, respectively.
3.3.3 Other carbonates: A polycarbonate suitable for smooth chemical recycle was engineered based on 1-benzyloxycarbonyl-3,4-epoxypyrrolidine (BEP) units [323]. In fact, a one-pot copolymerisation&#;depolymerisation cycle was enabled using a dinuclear salen&#;chromium complex in the presence of a bis(triphenylphosphine)iminium cocatalyst (Scheme 21). Therein, the BEP monomer was fully converted to the polycarbonate at 60 °C reaction temperature, while complete and selective depolymerisation back to BEP was achieved at 100 °C. The process could be repeated several times with no changes in either the monomer or the copolymer structure. After removing the catalyst, the polymer was stable at 200 °C for 10 h.
Polyamides may be natural (e.g., silk, wool) or synthetic polymers (e.g., nylons, aramids, polyaspartates) that are largely used in the manufacture of fibres and automotive components as well as in biomedicine, due to their excellent mechanical and thermal properties [324,325]. The widespread use of polyamides and the high price of the starting monomers, such as ε-caprolactam, have led to the development of several methods for their chemical recycling. Most of these are based on mineral acid [326], organic base (e.g., 4-dimethylaminopyridine, triethylenetetramine) [327,328] or organic acid (e.g., glycolic, lactic, benzoic acid) [329] catalysis, using supercritical methanol or ionic liquids as solvent [330]. Few literature reports exist on the depolymerisation of polyamides using metal catalysts. In an earlier paper, the hydrolysis of nylon-6 was achieved by a combination of zinc chloride (40 wt %) and phosphoric acid (20 wt %) under microwave irradiation, however, resulting in a mixture of linear and cyclic oligomers at 89% polymer conversion [121,331]. While drafting the present review, the first example of catalytic hydrogenative depolymerisation of polyamides and polyurethanes was described, using soluble Milstein-type Ru&#;pincer complexes (2 mol %), DMSO solvent and Kt-BuO cocatalyst at 150 °C and 70 bar H2 [332]. Typically, a selectivity to the corresponding diols/diamines/amino alcohols in the range of 20&#;80% was observed at 60&#;99% conversion, depending on the polymeric substrate. For instance, 6-amino-hexan-1-ol and BDM were obtained in 24% and 80% yield, respectively, from nylon-6 and the polyamide shown in Scheme 22.
Scheme 22: Hydrogenolysis of polyamides using soluble Ru catalysts.
Scheme 22: Hydrogenolysis of polyamides using soluble Ru catalysts.
Jump to Scheme 22
3.5.1 Epoxy resins (EP): EP are thermosetting polymers featuring high thermal and chemical resistance. They are widely used in the manufacture of paints, metal coatings, electronic components and adhesives [333]. EP are usually reinforced with fibres to give composite materials for the aeronautical, automotive and sport industries. Actually, recycling efforts of EP were mainly focused on the recovery of valuable (expensive) carbon fibres rather than the polymers themselves. Recently, a metal-catalysed route was reported for the degradation of the epoxy resin of bisphenol A diglycidyl ether (BADGE)&#;carbon fibres composites [334]. Therein, low-coordinated aquo ions of zinc enabled the selective cleavage of the R2CH&#;N bond while keeping intact RCH2&#;N, C&#;C and C&#;O bonds (Scheme 23). The method was previously adopted for the conversion of cellulose to hydroxymethylfurfural and required the use of highly soluble zinc chloride to obtain a concentrated aqueous solution of metal (60 wt % ZnCl2) [335]. On this basis, the small, incompletely coordinated Zn2+ ions were proposed to activate the selective cleavage of C&#;N bonds, acting as Lewis acid centres. The process carried out at 220 °C led to carbon fibres, a dimer of DGEBA reused for the synthesis of new EP, and 4,4'-methylenebis(2-methylcyclohexanol). The concentrated ZnCl2 solution showed good reusability, and thus adding some advantages to common highly energy-consuming methods.
Scheme 23: Catalytic depolymerisation of epoxy resin/carbon fibres composite.
Scheme 23: Catalytic depolymerisation of epoxy resin/carbon fibres composite.
Jump to Scheme 23
3.5.2 Polyethers: Polyethers are polymers with a solubility that depends heavily on the solvent used, including water, and they find applications in the cosmetic, pharmacy or paint industries [336]. Thermal decomposition or disposal into landfills are consolidated management systems of &#;end-of-life&#; polyethers [337,338], whereas very few studies cope with the catalytic depolymerisation through selective C&#;O bond cleavage into specific low-molecular-weight chemicals.
The group of Enthaler reported a number of research with a common strategy for polyethers depolymerisation [339-341]: Basically, the solvent-free reaction of a polyether with an acyl chloride in the presence of a catalytic amount (5 mol %) of zinc or iron salts as Lewis acid catalysts results in monomeric chloroesters, which are valuable chemicals reprocessable into other polymers (Scheme 24). A deep study was carried out investigating the effect of key reaction parameters: metal salt, catalyst loading, temperature, depolymerisation agent and the applicability to a variety of polyethers. Successful examples include depolymerisation of polyethylene glycol (PEG) and polytetrahydrofuran (polyTHF) to chloroesters in 70&#;78% and 92% yield, respectively, using ZnCl2 at 130 °C or Zn(OTf)2 catalyst when acetic anhydride was used as depolymerising agent [339,340]. Chloroester yields in the range 89&#;95% were obtained for PEG depolymerisation at 100 °C using FeCl2 as catalyst [341]. A mechanism was postulated in which the ether bond is cleaved via formation of an iron alkoxide intermediate (Scheme 25). Sustainability issues relate to the hazardous properties of low-molecular-weight acyl chlorides, which could be partially circumvented by the use of bioderived fatty acid chlorides [340].
Scheme 24: Depolymerisation of polyethers with metal salt catalysts and acyl chlorides.
Scheme 24: Depolymerisation of polyethers with metal salt catalysts and acyl chlorides.
Jump to Scheme 24
Scheme 25: Proposed mechanism for the iron-catalysed depolymerisation reaction of polyethers. Adapted with permission from [341], Copyright © WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim. Used with permission from Stephan Enthaler and Maik Weidauer, &#;Low&#;Temperature Iron&#;Catalysed Depolymerization of Polyethers&#;, ChemSusChem, John Wiley and Sons.
Scheme 25: Proposed mechanism for the iron-catalysed depolymerisation reaction of polyethers. Adapted with per...
Jump to Scheme 25
In a different approach, selective ring-closing depolymerisation of polyTHF to THF was achieved in 92% and 95% yield, respectively, using Lewis acid catalysis by FeCl3 (5 mol %, 180 °C) [342] or phosphotungstic acid (10 wt %, 130 °C) [343].