The market for "Poly(propylene carbonate) Market" is examined in this report, along with the factors that are expected to drive and restrain demand over the projected period.
If you are looking for more details, kindly visit SL Tec.
Introduction to Poly(propylene carbonate) Insights
Utilizing advanced data analytics, artificial intelligence, and machine learning algorithms, the gathering of insights for the Poly(propylene carbonate) Market has become increasingly futuristic. These technologies allow for real-time analysis of market dynamics, consumer behavior, and competitive landscape, enabling businesses to make informed decisions and stay ahead of the curve. The potential impact of these insights is significant, as they can help shape future market trends, identify emerging opportunities, and mitigate risks. The Poly(propylene carbonate) Market grows with a CAGR of 8.5% from to , highlighting the potential for substantial growth and innovation in the industry. By leveraging these futuristic approaches, stakeholders can adapt to changing market conditions, drive strategic growth, and ultimately, gain a competitive edge in the market.
Download a PDF sample of the Poly(propylene carbonate) Market Research Report https://www.reliableresearchreports.com/enquiry/request-sample/
Revolutionary Trends Shaping the Poly(propylene carbonate) Market Dynamics
1. Increased demand for eco-friendly materials: The shift towards sustainability has led to a growing demand for biodegradable and recyclable materials like poly(propylene carbonate).
2. Research and development in material science: Ongoing advancements in material science are leading to the development of new and improved poly(propylene carbonate) formulations with enhanced properties and performance.
3. Growing applications in various industries: The versatility of poly(propylene carbonate) has resulted in its increased use in industries such as packaging, automotive, and construction, driving market growth.
4. Investment in green technologies: Companies are investing in green technologies to produce poly(propylene carbonate) using environmentally friendly processes, aligning with consumer preferences for sustainable products.
Product Types Analysis in the Poly(propylene carbonate) Market
Poly(propylene carbonate) comes in various types such as Injection Molding Grade and Food Contact Grade. The Injection Molding Grade is ideal for manufacturing durable products with high precision while the Food Contact Grade ensures safety for packaging and storage of food items. The versatility and eco-friendly nature of Poly(propylene carbonate) make it appealing to industries like automotive, packaging, and consumer goods, driving demand in the market. Its unique features of high strength, heat resistance, and chemical stability attract consumers looking for sustainable and reliable solutions, ultimately boosting market growth and innovation.
Get all of your questions about the Poly(propylene carbonate) Market answered before purchasing it at https://www.reliableresearchreports.com/enquiry/pre-order-enquiry/
Product Applications and Market Growth Trends in the Poly(propylene carbonate) Market
Poly(propylene carbonate) is a versatile material with a wide range of applications. In biodegradable plastics, it is used as a sustainable alternative to traditional plastics, as it can break down in the environment, reducing plastics pollution. In the ceramic industry, it is utilized as a binder for ceramic materials, improving their strength and durability. In electronics, it is used as a dielectric material in capacitors, providing high insulation properties. The fastest-growing application segment is in biodegradable plastics, driven by increasing consumer awareness of environmental issues and the need for sustainable packaging solutions.
Transformational Impact of Poly(propylene carbonate) Market Disruptions
The Poly(propylene carbonate) market has experienced significant disruptions due to the impacts of COVID-19, accelerating digitalization trends, and industry convergence. The global pandemic has led to supply chain disruptions and decreased demand for certain products, affecting market dynamics. The rapid adoption of digital technologies has necessitated companies to enhance their online presence and digital marketing strategies. Additionally, industry convergence has driven collaborations and partnerships among companies from different sectors to offer innovative solutions. These disruptions are reshaping market strategies to focus on sustainability, innovation, and flexibility. Consumer behaviors also have shifted towards online shopping, remote work, and prioritizing health and safety. As a result, companies need to adapt to these changing trends by incorporating digital solutions and sustainable practices into their business models to remain competitive in the evolving market landscape.
Purchase the Comprehensive Report for Detailed Insights with Price of : https://www.reliableresearchreports.com/purchase/
Global Poly(propylene carbonate) Market Landscape and Future Pathways
The global Poly(propylene carbonate) Market is expected to witness significant growth in key regions such as North America, Europe, Asia-Pacific, Latin America, and Middle East & Africa. In North America, the United States and Canada are likely to drive market growth due to increasing demand for eco-friendly and sustainable products. In Europe, countries like Germany, France, and the UK are expected to play a crucial role in market expansion. The Asia-Pacific region, particularly China, Japan, South Korea, and India, is anticipated to emerge as key growth markets for Poly(propylene carbonate) due to rapid industrialization and favorable government initiatives. Additionally, Latin America and Middle East & Africa, including Mexico, Brazil, Turkey, and the UAE, are projected to witness substantial growth opportunities. Regulatory shifts towards promoting sustainable materials are likely to further influence market trajectories and drive innovation in the Poly(propylene carbonate) market.
Purchase this report here: https://www.reliableresearchreports.com/purchase/
Innovative Competitive Intelligence Strategies of Poly(propylene carbonate) Market Share
In the competitive landscape of Poly(propylene carbonate) (PPC) market, companies like Empower Materials, SK Energy, Novomer, BASF, Cardia Bioplastics, Tianguan, Bangfeng, Jiangsu Zhongke Jinlong-CAS Chemical, and Inner Mongolia Mengxi High-Tech can leverage AI-powered market scanning to gather real-time insights on competitors' activities, product launches, pricing strategies, and customer preferences. By analyzing data from various sources, these companies can anticipate competitor moves and identify potential threats or opportunities in the market.
Additionally, predictive analytics can help in forecasting market trends, customer demand, and competitor behavior, enabling companies to make data-driven decisions and stay ahead of the competition. By utilizing dynamic pricing models, businesses can adjust their pricing strategies in response to competitor actions, market changes, and customer demand, ensuring maximum profitability and market share.
Overall, these competitive intelligence strategies give businesses a competitive edge by enabling them to make informed decisions, anticipate competitor moves, and respond quickly to market dynamics, ultimately driving growth and success in the PPC market.
Poly(propylene carbonate) Market Expansion Tactics and Growth Forecasts
Innovative expansion tactics for the Poly(propylene carbonate) Market include cross-industry collaborations with automotive, electronics, and healthcare sectors to leverage its unique properties such as biodegradability and high chemical resistance. Ecosystem partnerships with waste management companies and sustainability initiatives can drive demand for environmentally-friendly products. Disruptive product launches like bio-based alternatives to traditional plastics can further propel market growth.
Forecasts suggest that the Poly(propylene carbonate) Market will experience significant growth driven by these strategies and industry trends. Market value is expected to increase at a steady rate, with a CAGR of around 7% over the next five years. With increasing awareness of the environmental impact of traditional plastics, the demand for sustainable alternatives like Poly(propylene carbonate) is expected to surge, driving market expansion and innovation.
Purchase this Report: https://www.reliableresearchreports.com/purchase/
Check more reports on https://www.reliableresearchreports.com/
Over the last two decades, there has been a significant effort to improve reliability, efficiency and manufacturability of photovoltaics (PV).
Most of this effort has been targeted towards the PV&#;s front-side construction, including contact formation with glasses and metallization. To that end, extensive advancements have been made to optimize the application of front-side conductive architecture so as to realize the highest quality of end product with superior manufacturing capacities.
Image Credits: shutterstock.com/Bohbeh
Silver pastes are often used on the front-side architecture of a solar cell. These pastes are heterogeneous mixtures comprising of metallic silver flakes or powders, organic binders, glass frits, and other additives like dispersant/surfactants, plasticizers, solvents and the like. The silver-bearing part of the front-side paste constitutes a flake type powder, a spheroidal powder, or a combination of the two. The frit component of the pastes does not contain lead, and provides a range of CTE and Tg, in addition to particle size and distribution. Both the performance and quality of the front-side design of a solar cell are governed by these two material sets.
While the organic phase of the front-side solar paste plays a major role, it is often consigned to the transference of the imparted structural design, and how well the paste is able to process during the course of printing. Although a wide range of materials is available for the organic phase of the front-side solar paste, most commercially available systems only belong to a few categories &#; acrylics, cellulosics, and rosinates.
The market for "Poly(propylene carbonate) Market" is examined in this report, along with the factors that are expected to drive and restrain demand over the projected period.
Introduction to Poly(propylene carbonate) Insights
Utilizing advanced data analytics, artificial intelligence, and machine learning algorithms, the gathering of insights for the Poly(propylene carbonate) Market has become increasingly futuristic. These technologies allow for real-time analysis of market dynamics, consumer behavior, and competitive landscape, enabling businesses to make informed decisions and stay ahead of the curve. The potential impact of these insights is significant, as they can help shape future market trends, identify emerging opportunities, and mitigate risks. The Poly(propylene carbonate) Market grows with a CAGR of 8.5% from to , highlighting the potential for substantial growth and innovation in the industry. By leveraging these futuristic approaches, stakeholders can adapt to changing market conditions, drive strategic growth, and ultimately, gain a competitive edge in the market.
Download a PDF sample of the Poly(propylene carbonate) Market Research Report https://www.reliableresearchreports.com/enquiry/request-sample/
Revolutionary Trends Shaping the Poly(propylene carbonate) Market Dynamics
1. Increased demand for eco-friendly materials: The shift towards sustainability has led to a growing demand for biodegradable and recyclable materials like poly(propylene carbonate).
2. Research and development in material science: Ongoing advancements in material science are leading to the development of new and improved poly(propylene carbonate) formulations with enhanced properties and performance.
3. Growing applications in various industries: The versatility of poly(propylene carbonate) has resulted in its increased use in industries such as packaging, automotive, and construction, driving market growth.
4. Investment in green technologies: Companies are investing in green technologies to produce poly(propylene carbonate) using environmentally friendly processes, aligning with consumer preferences for sustainable products.
Product Types Analysis in the Poly(propylene carbonate) Market
Poly(propylene carbonate) comes in various types such as Injection Molding Grade and Food Contact Grade. The Injection Molding Grade is ideal for manufacturing durable products with high precision while the Food Contact Grade ensures safety for packaging and storage of food items. The versatility and eco-friendly nature of Poly(propylene carbonate) make it appealing to industries like automotive, packaging, and consumer goods, driving demand in the market. Its unique features of high strength, heat resistance, and chemical stability attract consumers looking for sustainable and reliable solutions, ultimately boosting market growth and innovation.
Get all of your questions about the Poly(propylene carbonate) Market answered before purchasing it at https://www.reliableresearchreports.com/enquiry/pre-order-enquiry/
Product Applications and Market Growth Trends in the Poly(propylene carbonate) Market
Poly(propylene carbonate) is a versatile material with a wide range of applications. In biodegradable plastics, it is used as a sustainable alternative to traditional plastics, as it can break down in the environment, reducing plastics pollution. In the ceramic industry, it is utilized as a binder for ceramic materials, improving their strength and durability. In electronics, it is used as a dielectric material in capacitors, providing high insulation properties. The fastest-growing application segment is in biodegradable plastics, driven by increasing consumer awareness of environmental issues and the need for sustainable packaging solutions.
Transformational Impact of Poly(propylene carbonate) Market Disruptions
The Poly(propylene carbonate) market has experienced significant disruptions due to the impacts of COVID-19, accelerating digitalization trends, and industry convergence. The global pandemic has led to supply chain disruptions and decreased demand for certain products, affecting market dynamics. The rapid adoption of digital technologies has necessitated companies to enhance their online presence and digital marketing strategies. Additionally, industry convergence has driven collaborations and partnerships among companies from different sectors to offer innovative solutions. These disruptions are reshaping market strategies to focus on sustainability, innovation, and flexibility. Consumer behaviors also have shifted towards online shopping, remote work, and prioritizing health and safety. As a result, companies need to adapt to these changing trends by incorporating digital solutions and sustainable practices into their business models to remain competitive in the evolving market landscape.
Purchase the Comprehensive Report for Detailed Insights with Price of : https://www.reliableresearchreports.com/purchase/
Global Poly(propylene carbonate) Market Landscape and Future Pathways
The global Poly(propylene carbonate) Market is expected to witness significant growth in key regions such as North America, Europe, Asia-Pacific, Latin America, and Middle East & Africa. In North America, the United States and Canada are likely to drive market growth due to increasing demand for eco-friendly and sustainable products. In Europe, countries like Germany, France, and the UK are expected to play a crucial role in market expansion. The Asia-Pacific region, particularly China, Japan, South Korea, and India, is anticipated to emerge as key growth markets for Poly(propylene carbonate) due to rapid industrialization and favorable government initiatives. Additionally, Latin America and Middle East & Africa, including Mexico, Brazil, Turkey, and the UAE, are projected to witness substantial growth opportunities. Regulatory shifts towards promoting sustainable materials are likely to further influence market trajectories and drive innovation in the Poly(propylene carbonate) market.
Purchase this report here: https://www.reliableresearchreports.com/purchase/
Innovative Competitive Intelligence Strategies of Poly(propylene carbonate) Market Share
In the competitive landscape of Poly(propylene carbonate) (PPC) market, companies like Empower Materials, SK Energy, Novomer, BASF, Cardia Bioplastics, Tianguan, Bangfeng, Jiangsu Zhongke Jinlong-CAS Chemical, and Inner Mongolia Mengxi High-Tech can leverage AI-powered market scanning to gather real-time insights on competitors' activities, product launches, pricing strategies, and customer preferences. By analyzing data from various sources, these companies can anticipate competitor moves and identify potential threats or opportunities in the market.
Additionally, predictive analytics can help in forecasting market trends, customer demand, and competitor behavior, enabling companies to make data-driven decisions and stay ahead of the competition. By utilizing dynamic pricing models, businesses can adjust their pricing strategies in response to competitor actions, market changes, and customer demand, ensuring maximum profitability and market share.
Overall, these competitive intelligence strategies give businesses a competitive edge by enabling them to make informed decisions, anticipate competitor moves, and respond quickly to market dynamics, ultimately driving growth and success in the PPC market.
Poly(propylene carbonate) Market Expansion Tactics and Growth Forecasts
Innovative expansion tactics for the Poly(propylene carbonate) Market include cross-industry collaborations with automotive, electronics, and healthcare sectors to leverage its unique properties such as biodegradability and high chemical resistance. Ecosystem partnerships with waste management companies and sustainability initiatives can drive demand for environmentally-friendly products. Disruptive product launches like bio-based alternatives to traditional plastics can further propel market growth.
Forecasts suggest that the Poly(propylene carbonate) Market will experience significant growth driven by these strategies and industry trends. Market value is expected to increase at a steady rate, with a CAGR of around 7% over the next five years. With increasing awareness of the environmental impact of traditional plastics, the demand for sustainable alternatives like Poly(propylene carbonate) is expected to surge, driving market expansion and innovation.
Purchase this Report: https://www.reliableresearchreports.com/purchase/
Check more reports on https://www.reliableresearchreports.com/
Over the last two decades, there has been a significant effort to improve reliability, efficiency and manufacturability of photovoltaics (PV).
Most of this effort has been targeted towards the PV&#;s front-side construction, including contact formation with glasses and metallization. To that end, extensive advancements have been made to optimize the application of front-side conductive architecture so as to realize the highest quality of end product with superior manufacturing capacities.
Image Credits: shutterstock.com/Bohbeh
Silver pastes are often used on the front-side architecture of a solar cell. These pastes are heterogeneous mixtures comprising of metallic silver flakes or powders, organic binders, glass frits, and other additives like dispersant/surfactants, plasticizers, solvents and the like. The silver-bearing part of the front-side paste constitutes a flake type powder, a spheroidal powder, or a combination of the two. The frit component of the pastes does not contain lead, and provides a range of CTE and Tg, in addition to particle size and distribution. Both the performance and quality of the front-side design of a solar cell are governed by these two material sets.
While the organic phase of the front-side solar paste plays a major role, it is often consigned to the transference of the imparted structural design, and how well the paste is able to process during the course of printing. Although a wide range of materials is available for the organic phase of the front-side solar paste, most commercially available systems only belong to a few categories &#; acrylics, cellulosics, and rosinates.
Figure 1 illustrates a few basic binder materials together with polypropylene carbonate derived from the polyalkylene carbonate group of materials. The polymeric range can be made to offer different molecular weights, which can impart degrees of control of organic rheology. The rosin range of binders originates from a fundamental building unit of abietic acid. As such, the rosins are often hydrogenated to prevent unsaturation, and are either utilized in this form, or reacted to form different esterified versions of hydrogenated rosins.
Figure 1. Chemical structure representations of binder materials for pastes. A: hydroxyethyl cellulose, B: a rosinate, C: an acrylic, D: polypropylene carbonate.
The general composition of the materials, together with the chemical formula and corresponding degrees of unsaturation are listed in Table 1. The materials&#; composition and structure play a major role in how they impart the preferred fluid properties and render the interaction with solid phases in a paste during printing and firing processes.
Table 1. Hydrocarbon composition of structures of Figure 1
Material Name Composition Chemical Formula Degrees of Unsaturation C (Wt.%) H (Wt.%) O (Wt.% Hydroxyethyl Cellulose ~48 ~8 ~44 C14H27O10 1.5 Rosinate ~78 ~12 ~10 C20H34O2 4 Acrylic ~65 ~10 ~25 C7H14O2 1 Polypropylene Carbonate ~54 ~10 ~36 C6H12O3 1Generally, rheological characteristics of front-side solar pastes are shear-thinning, non-Newtonian, thixotropic fluids. A paste is formulated by different mixing and milling processes, integrating individual components to obtain the required viscosity response with related solids content, and at the same time acquiring controlled and repeatable performance during the application and processing protocols. This article aims to show the drop-in-replacement compatibility of a clean-burning binder systems, with traditional material sets to manufacture PV cells that are similar to existing modern expectations.
A thick film paste was used to assess a finished PV cell. This paste was developed from QPAC®, a polycarbonate-based binder system from Empower Materials. For the additional solvent, propylene carbonate was used. Then, using a mixture of spherical and flake powders (PV-2 and SF-3), the silver phase of the clean-burning binder paste was made. Dispersing agents and plasticizer were used to provide excellent paste properties and processability. A lead-free glass composition was also used. Table 2 shows the composition of the thick film paste used in this analysis.
Table 2. Thick film paste composition with clean-burning binder
Component Name Composition (Wt.%) Silver 86.2 Glass 4.5 Dispersant & Plasticizer 3.7 QPAC®
40 Binder 3.6 Solvent 2.0In order to develop the QPAC®40-based binder paste system, the silver components were mixed with the solvent, plasticizer, and dispersant by means of a non-contact planetary mixer. Once the initial mixing was complete, the QPAC®40 binder solution was introduced, and the mixing program was performed again. As soon as the second mixing process was over, the glass component was added and the mixing program was again repeated for 12 minutes. The finished paste was simultaneously assessed and compared with other commercially available systems, designated as Paste A and Paste B.
A Brookfield Engineering HBTD, equipped with a cone and plate type spindle (CP-52), was used to determine the paste quality metrics at 25 °C for stress and viscosity, and a Hegman Gauge was used for fineness of grind (FOG). Next, thermal analysis was carried out by means of a Mettler Toledo STAR TGA/DSC at 10 °C.min-1 in air with ceramic pans, and screen printing was carried out with a Baccini Softline printer with speed of 100 mm.s-1, squeegee pressure of 75 N, and snap off of 1.2 mm. Printing was done on 239 cm2 mono-Si wafers, and all samples were applied with commercial rear tabbing pastes. Firing was done using the model CF-SL six-zone oven supplied by Despatch Industries.
Series Resistance, Efficiency, Solar cell VOC, ISC, FF, and Shunt Resistance were determined by means of a Solar Cell I-V Curve Measurement System IV16L with a class-AAA solar simulator, equipped with continuous 16 x 16 cm beam, Air Mass 1.5 Global (AM1.5G) spectral filtering. The entire cell measurements were carried out after calibration with the National Renewable Energy Laboratory-certified solar cell.
There are several preferred features for a thick film paste to be used for front-side PV. These features include dispersion stability, material component homogeneity, high solids content, screen printing performance, and rheology. These are all interrelated parameters which prove useful for determining the paste quality for its desired application. The FOG of individual paste system is compared in Table 3.
Table 3. FOG comparison of paste samples
FOG Parameter Paste Sample QPAC A B 1st Scratch (µm) 5.5 8.3 5.5 3rd Scratch (µm) 4.2 4.1 5.3 Main Break 1.4 2.1 1.8These results demonstrate that these pastes are roughly the same with respect to their dispersion state. Standard methods used for producing front-side solar pastes feature a milling step that is done with three roll milling. A non-contact planetary mixer method (Thinky AR250) was used to develop the QPAC®40 paste. The FOG results thus obtained demonstrate that end processing of the components for the QPAC®40 paste is perfect for the paste fabrication process. The final rheology of the pastes was very similar, as shown in Figure 2 which compares the stress and viscosity responses of the final pastes. A subtle variation was seen in the viscosity responses between the &#;A&#; and QPAC®40 samples when compared to the &#;B&#; sample over a 0.25 s-1 shear rate, whilst significant variations were seen in the stress responses of each individual paste sample. This is due to the presence of different components in the pastes, such as glass materials, variations in particle shape and size of the silver powder, other additives, and the general organic composition.
Figure 2. Viscosity (left) and Stress (right) vs. shear rate of each thick film paste.
The organic components of thick film pastes applied on the front-side architecture of the solar cell were predicted to allow retention of the imparted geometry, but were fully removed during the course of the firing process so that both the metal and glass could reach their optimal final phase without impacting the mechanisms of phase formation. Figure 3 shows the differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) responses of the individual pastes assessed in this analysis.
Figure 3. TGA (left) and DSC (right) traces of each thick film paste. Thermal scan performed in air at 10 °C.min-1.
It was observed that each paste had analogous properties with regards to the loss of solvent and other onsets of organic component decomposition. Overall mass changes were also similar, but did not occur in the same temperature region. Paste A and B exhibited on-going mass loss as a result of decomposition until ~400 °C, while the QPAC®40 based paste exhibited almost complete removal at 300 °C temperature. Extensive retention of organic decomposition was seen in Paste A and B TGA traces to over 650 °C. Table 4 shows the comparison of mass changes for all pastes at 50 °C increments from 300 to 630 °C.
Table 4. TGA summary of thick film paste comparison
Temperature®
40 PasteWhile similarity was again observed in the shape of the heat flow curves obtained from the thermal decomposition analysis of individual paste sample, the heat flow energy failed to occur in the same thermal region. In the QPAC®40 based paste, an exothermic peak was seen at 280 °C, while in Paste A and B, exothermic excursions were seen at 335 °C and 310 °C, respectively, along with extra decomposition daughter exotherms over these temperatures. Finally, both Pastes A and B had a signal of about 600 °C, relating to a TGA mass loss of 0.1 to 0.2 Wt.%, showing intense carbonaceous residue experiencing final decomposition in the thermal profile. The heat flow data shows the differences of individual paste sample experiencing the same thermal profile (Figure 4).
Figure 4. Representation of the rate of change of energy during exposure of each paste sample to the same linear thermal profile in air.
Scanning electron microscopy of the finger lines and bus bars was done on the planar view of the fired and printed wafers, and the same was done on the fracture cross sections of the finger lines. The same areas of bus bars and finger lines were investigated from individual set of fired and printed wafers representing individual paste types. The representative images from these results are shown in Figure 5. From Column 1 and 2 images, it is possible to determine the line widths as 84 µm, 95 µm and 105 µm for the QPAC®-based paste, Paste A, and Paste B respectively. When the finger lines and bus bars were subjected to high magnification analysis, a major difference was seen in the pore/void concentration on the fired and printed surface features of each individual paste sample (Column 3, Figure 5). In the final bulk lines of individual paste sample, no major cosmetic differences were observed.
Figure 5. SEM images of finger lines from each paste (after firing).
The finger lines&#; fracture-cross sections from individual paste sample are illustrated in Columns 4 and 5 of Figure 5. In fact, the 5,000X magnification images seen in Column 5 show marked variations between Paste A and B and the QPAC®40 based paste. In Paste A and B, intensive cross section pore/void spaces are seen in the finger line body spanning from the wafer interface to all surfaces of the finger line. Conversely, superior interface properties are seen in both Paste A and B between the wafer and the conductive finger line. In the case of the QPAC®40 based paste, no pore/void space is seen in the finger line body, but poor interfacing are seen at the wafer interface and conductive finger line.
The electrical testing data of individual pastes compared in this analysis is shown in Table 5. The &#;Suns-VOC&#; data shows closely similar results of individual paste samples in this analysis.
Table 5. Summary of electrical testing results
Parameter Units Sample QPAC®
40 Based Paste Paste A Paste B Suns-VOC Pseudo Efficiency (%) 18.0% 18.5% 18.5% pFF (%) 79.4% 81.3% 81.0% RSHUNT (Ω cm2, Fitted) .7 Ideality Factor 1 Sun 1.01 1.08 1.08 0.1 Sun 1.60 1.16 1.24 JO1 (A.cm-2x10-12) 2.20 2.20 2.10 JO2 (A.cm-2x10-12) 6.70 3.10 3.16 Contact Resistance Sheet Resistivity (Ω/sq) 73.2 74.1 73.7 Contact Resistance (Ω) 14.85 0.03 0.02 Transfer Length (cm) 0. 0. 0. Contact Resistivity (Ω cm-2) 2. 0. 0. Fit R2 0.997 1.000 1.000 Light I-V Performance VOc (V) 0.608 0.615 0.613 JSC (mA.cm-2) 37.65 36.61 36.35 FF (%) 66.7 78.7 79.6 Efficiency (%) 15.29 17.70 17.74 RSERIES (Ω cm2) 2.88 0.65 0.54 RSHUNT (Ω cm2)The 1-Sun Ideality Factor or M-Factor indicates better performance in comparison to either Paste A or B, showing stronger junction etching with respect to the QPAC® based paste sample. The &#;Contact Resistance&#; results summarized in Table 5 revealed reproducible junction sheet resistance, but the resistivity and contact resistance display poorer performance when compared to Paste A or B. This data shows that the QPAC®40 paste sample did not diffuse into the wafer adequately, and thus confirmed the above-discussed SEM results. Paste A and B showed excellent performance. Similarly, the QPAC®40 paste sample had desirable characteristics, but reduced junction etching.
The front-side solar cell thick film paste sample was developed using a clean-burning binder system. The properties of the pastes were compared with other pastes that are commercially available in the market, and were found to have almost identical properties, such as FOG, rheology, and solids loading. Thermal analysis of the commercial systems, in contrast to the paste sample, showed that the former had a wide decomposition range and the presence of residual carbonaceous material as high as 630 °C, while the QPAC®40 based paste offers complete organic phase burn-out by 300 °C in air. Comparison was also made of the final microstructure and cosmetic features of the fired and printed structures on the front-side of solar cells. While the commercial paste samples were similar to each other in terms of electrical testing, the QPAC®40 based paste exhibited excellent qualities but showed poorer electrical performance as a result of reduced junction etching. However, if a different glass component is used in the formulation, this limitation can be resolved.
This information has been sourced, reviewed and adapted from materials provided by Empower Materials.
For more information on this source, please visit Empower Materials.
Figure 1 illustrates a few basic binder materials together with polypropylene carbonate derived from the polyalkylene carbonate group of materials. The polymeric range can be made to offer different molecular weights, which can impart degrees of control of organic rheology. The rosin range of binders originates from a fundamental building unit of abietic acid. As such, the rosins are often hydrogenated to prevent unsaturation, and are either utilized in this form, or reacted to form different esterified versions of hydrogenated rosins.
Figure 1. Chemical structure representations of binder materials for pastes. A: hydroxyethyl cellulose, B: a rosinate, C: an acrylic, D: polypropylene carbonate.
The general composition of the materials, together with the chemical formula and corresponding degrees of unsaturation are listed in Table 1. The materials&#; composition and structure play a major role in how they impart the preferred fluid properties and render the interaction with solid phases in a paste during printing and firing processes.
Table 1. Hydrocarbon composition of structures of Figure 1
Material Name Composition Chemical Formula Degrees of Unsaturation C (Wt.%) H (Wt.%) O (Wt.% Hydroxyethyl Cellulose ~48 ~8 ~44 C14H27O10 1.5 Rosinate ~78 ~12 ~10 C20H34O2 4 Acrylic ~65 ~10 ~25 C7H14O2 1 Polypropylene Carbonate ~54 ~10 ~36 C6H12O3 1Generally, rheological characteristics of front-side solar pastes are shear-thinning, non-Newtonian, thixotropic fluids. A paste is formulated by different mixing and milling processes, integrating individual components to obtain the required viscosity response with related solids content, and at the same time acquiring controlled and repeatable performance during the application and processing protocols. This article aims to show the drop-in-replacement compatibility of a clean-burning binder systems, with traditional material sets to manufacture PV cells that are similar to existing modern expectations.
A thick film paste was used to assess a finished PV cell. This paste was developed from QPAC®, a polycarbonate-based binder system from Empower Materials. For the additional solvent, propylene carbonate was used. Then, using a mixture of spherical and flake powders (PV-2 and SF-3), the silver phase of the clean-burning binder paste was made. Dispersing agents and plasticizer were used to provide excellent paste properties and processability. A lead-free glass composition was also used. Table 2 shows the composition of the thick film paste used in this analysis.
Table 2. Thick film paste composition with clean-burning binder
Component Name Composition (Wt.%) Silver 86.2 Glass 4.5 Dispersant & Plasticizer 3.7 QPAC®
40 Binder 3.6 Solvent 2.0In order to develop the QPAC®40-based binder paste system, the silver components were mixed with the solvent, plasticizer, and dispersant by means of a non-contact planetary mixer. Once the initial mixing was complete, the QPAC®40 binder solution was introduced, and the mixing program was performed again. As soon as the second mixing process was over, the glass component was added and the mixing program was again repeated for 12 minutes. The finished paste was simultaneously assessed and compared with other commercially available systems, designated as Paste A and Paste B.
A Brookfield Engineering HBTD, equipped with a cone and plate type spindle (CP-52), was used to determine the paste quality metrics at 25 °C for stress and viscosity, and a Hegman Gauge was used for fineness of grind (FOG). Next, thermal analysis was carried out by means of a Mettler Toledo STAR TGA/DSC at 10 °C.min-1 in air with ceramic pans, and screen printing was carried out with a Baccini Softline printer with speed of 100 mm.s-1, squeegee pressure of 75 N, and snap off of 1.2 mm. Printing was done on 239 cm2 mono-Si wafers, and all samples were applied with commercial rear tabbing pastes. Firing was done using the model CF-SL six-zone oven supplied by Despatch Industries.
Series Resistance, Efficiency, Solar cell VOC, ISC, FF, and Shunt Resistance were determined by means of a Solar Cell I-V Curve Measurement System IV16L with a class-AAA solar simulator, equipped with continuous 16 x 16 cm beam, Air Mass 1.5 Global (AM1.5G) spectral filtering. The entire cell measurements were carried out after calibration with the National Renewable Energy Laboratory-certified solar cell.
There are several preferred features for a thick film paste to be used for front-side PV. These features include dispersion stability, material component homogeneity, high solids content, screen printing performance, and rheology. These are all interrelated parameters which prove useful for determining the paste quality for its desired application. The FOG of individual paste system is compared in Table 3.
Table 3. FOG comparison of paste samples
FOG Parameter Paste Sample QPAC A B 1st Scratch (µm) 5.5 8.3 5.5 3rd Scratch (µm) 4.2 4.1 5.3 Main Break 1.4 2.1 1.8These results demonstrate that these pastes are roughly the same with respect to their dispersion state. Standard methods used for producing front-side solar pastes feature a milling step that is done with three roll milling. A non-contact planetary mixer method (Thinky AR250) was used to develop the QPAC®40 paste. The FOG results thus obtained demonstrate that end processing of the components for the QPAC®40 paste is perfect for the paste fabrication process. The final rheology of the pastes was very similar, as shown in Figure 2 which compares the stress and viscosity responses of the final pastes. A subtle variation was seen in the viscosity responses between the &#;A&#; and QPAC®40 samples when compared to the &#;B&#; sample over a 0.25 s-1 shear rate, whilst significant variations were seen in the stress responses of each individual paste sample. This is due to the presence of different components in the pastes, such as glass materials, variations in particle shape and size of the silver powder, other additives, and the general organic composition.
Figure 2. Viscosity (left) and Stress (right) vs. shear rate of each thick film paste.
The organic components of thick film pastes applied on the front-side architecture of the solar cell were predicted to allow retention of the imparted geometry, but were fully removed during the course of the firing process so that both the metal and glass could reach their optimal final phase without impacting the mechanisms of phase formation. Figure 3 shows the differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) responses of the individual pastes assessed in this analysis.
Figure 3. TGA (left) and DSC (right) traces of each thick film paste. Thermal scan performed in air at 10 °C.min-1.
It was observed that each paste had analogous properties with regards to the loss of solvent and other onsets of organic component decomposition. Overall mass changes were also similar, but did not occur in the same temperature region. Paste A and B exhibited on-going mass loss as a result of decomposition until ~400 °C, while the QPAC®40 based paste exhibited almost complete removal at 300 °C temperature. Extensive retention of organic decomposition was seen in Paste A and B TGA traces to over 650 °C. Table 4 shows the comparison of mass changes for all pastes at 50 °C increments from 300 to 630 °C.
Table 4. TGA summary of thick film paste comparison
Temperature®
40 PasteWhile similarity was again observed in the shape of the heat flow curves obtained from the thermal decomposition analysis of individual paste sample, the heat flow energy failed to occur in the same thermal region. In the QPAC®40 based paste, an exothermic peak was seen at 280 °C, while in Paste A and B, exothermic excursions were seen at 335 °C and 310 °C, respectively, along with extra decomposition daughter exotherms over these temperatures. Finally, both Pastes A and B had a signal of about 600 °C, relating to a TGA mass loss of 0.1 to 0.2 Wt.%, showing intense carbonaceous residue experiencing final decomposition in the thermal profile. The heat flow data shows the differences of individual paste sample experiencing the same thermal profile (Figure 4).
Figure 4. Representation of the rate of change of energy during exposure of each paste sample to the same linear thermal profile in air.
Scanning electron microscopy of the finger lines and bus bars was done on the planar view of the fired and printed wafers, and the same was done on the fracture cross sections of the finger lines. The same areas of bus bars and finger lines were investigated from individual set of fired and printed wafers representing individual paste types. The representative images from these results are shown in Figure 5. From Column 1 and 2 images, it is possible to determine the line widths as 84 µm, 95 µm and 105 µm for the QPAC®-based paste, Paste A, and Paste B respectively. When the finger lines and bus bars were subjected to high magnification analysis, a major difference was seen in the pore/void concentration on the fired and printed surface features of each individual paste sample (Column 3, Figure 5). In the final bulk lines of individual paste sample, no major cosmetic differences were observed.
Figure 5. SEM images of finger lines from each paste (after firing).
The finger lines&#; fracture-cross sections from individual paste sample are illustrated in Columns 4 and 5 of Figure 5. In fact, the 5,000X magnification images seen in Column 5 show marked variations between Paste A and B and the QPAC®40 based paste. In Paste A and B, intensive cross section pore/void spaces are seen in the finger line body spanning from the wafer interface to all surfaces of the finger line. Conversely, superior interface properties are seen in both Paste A and B between the wafer and the conductive finger line. In the case of the QPAC®40 based paste, no pore/void space is seen in the finger line body, but poor interfacing are seen at the wafer interface and conductive finger line.
The electrical testing data of individual pastes compared in this analysis is shown in Table 5. The &#;Suns-VOC&#; data shows closely similar results of individual paste samples in this analysis.
Table 5. Summary of electrical testing results
Parameter Units Sample QPAC®
40 Based Paste Paste A Paste B Suns-VOC Pseudo Efficiency (%) 18.0% 18.5% 18.5% pFF (%) 79.4% 81.3% 81.0% RSHUNT (Ω cm2, Fitted) .7 Ideality Factor 1 Sun 1.01 1.08 1.08 0.1 Sun 1.60 1.16 1.24 JO1 (A.cm-2x10-12) 2.20 2.20 2.10 JO2 (A.cm-2x10-12) 6.70 3.10 3.16 Contact Resistance Sheet Resistivity (Ω/sq) 73.2 74.1 73.7 Contact Resistance (Ω) 14.85 0.03 0.02 Transfer Length (cm) 0. 0. 0. Contact Resistivity (Ω cm-2) 2. 0. 0. Fit R2 0.997 1.000 1.000 Light I-V Performance VOc (V) 0.608 0.615 0.613 JSC (mA.cm-2) 37.65 36.61 36.35 FF (%) 66.7 78.7 79.6 Efficiency (%) 15.29 17.70 17.74 RSERIES (Ω cm2) 2.88 0.65 0.54 RSHUNT (Ω cm2)The 1-Sun Ideality Factor or M-Factor indicates better performance in comparison to either Paste A or B, showing stronger junction etching with respect to the QPAC® based paste sample. The &#;Contact Resistance&#; results summarized in Table 5 revealed reproducible junction sheet resistance, but the resistivity and contact resistance display poorer performance when compared to Paste A or B. This data shows that the QPAC®40 paste sample did not diffuse into the wafer adequately, and thus confirmed the above-discussed SEM results. Paste A and B showed excellent performance. Similarly, the QPAC®40 paste sample had desirable characteristics, but reduced junction etching.
The front-side solar cell thick film paste sample was developed using a clean-burning binder system. The properties of the pastes were compared with other pastes that are commercially available in the market, and were found to have almost identical properties, such as FOG, rheology, and solids loading. Thermal analysis of the commercial systems, in contrast to the paste sample, showed that the former had a wide decomposition range and the presence of residual carbonaceous material as high as 630 °C, while the QPAC®40 based paste offers complete organic phase burn-out by 300 °C in air. Comparison was also made of the final microstructure and cosmetic features of the fired and printed structures on the front-side of solar cells. While the commercial paste samples were similar to each other in terms of electrical testing, the QPAC®40 based paste exhibited excellent qualities but showed poorer electrical performance as a result of reduced junction etching. However, if a different glass component is used in the formulation, this limitation can be resolved.
This information has been sourced, reviewed and adapted from materials provided by Empower Materials.
For more information on this source, please visit Empower Materials.
Want more information on MMA Plant? Feel free to contact us.